Can also be furnished:
No. 3 Finish - Polished One or Two Sides
No. 4 Finish - Polished One or Two Sides
Non-Magnetic (May be Slightly magnetic when cold worked)
Paper Interleaved or Vinyl Masked:
22 Gauge and Heavier
A.S.T.M. A480/A240 ASME SA-240
A.S.T.M. A262 Prac E
Specifications
Material |
N/A Type 317L Stainless Steel |
Shapeform |
N/A Coil |
Thickness |
N/A 19 gauge |
Thickness |
N/A 0.042 inches1.0668 mm |
Size |
N/A 48 x Coil |
Width |
N/A 48 |
Sheet Weight per Unit Area |
N/A 1.764 lbs/ft²8.611848 kg/m² |
Finish |
N/A No. 2B No. 3 No. 4 |
Condition |
N/A Cold Rolled Annealed |
Nominal Composition |
N/A 0.08% Max. Carbon 1.00% Max. Silicon 11.00 to 15.00% Nickel 18.00 to 20.00% Chrominum 2.0 to 3.0% Molybdenum 2.00% Max. Manganese |
ASTM Specification |
N/A ASTM A240 ASTM A262 Prac E ASTM A480 ASTM SA-240 UNS S31700 |
Typical Mechanical Properties
Steel Alloy Group |
N/A Austenitic |
Magnetic Properties |
N/A Non-Magnetic |
Harden By |
N/A Cold Work |
Corrosion Resistance |
N/A High |
Hardness |
N/A Low to Med. |
Strength |
N/A Low to Med. |
Ductility |
N/A High |
Toughness |
N/A High |
Elec. Conductance |
N/A Low |
Thermal Conductance |
N/A Low |
Thermal Expansion |
N/A High |
Heat Resistance (Scaling Strength) |
N/A High/High |
Comparative Characteristics and Applications
Density |
N/A 0.29 lbs/in³ |
Modulus of Elasticity in Tension |
N/A 28.0 x 106 lbs/in² |
Specific Heat (32 to 212°F) |
N/A 0.12 BTU/ºF/lbs |
Thermal Conductivity at 212°F |
N/A 9.4 BTU/hr.ft²/ft/ºF |
Thermal Conductivity at 932°F |
N/A 12.4 BTU/hr.ft²/ft/ºF |
Mean Coefficient of Thermal Expansion per °F (32 to 212°F) |
N/A 8.9 x 10-6 ºF |
Mean Coefficient of Thermal Expansion per °F (32 to 600°F) |
N/A 9.0 x 10-6 ºF |
Mean Coefficient of Thermal Expansion per °F (32 to 1000°F) |
N/A 9.7 x 10-6 ºF |
Mean Coefficient of Thermal Expansion per °F (32 to 1200°F) |
N/A 10.3 x 10-6 ºF |
Melting Point Range |
N/A 2500 to 2550 ºF |
Electrical Resistivity |
N/A 74 µΩ.cm |
Max. Operating Temp. (Continuous Service) |
N/A 1700 ºF |
Max. Operating Temp. (Intermittent Service) |
N/A 1600 ºF |
Welding Properties |
N/A Very Good-Tough Welds |
Drawing and Stamping |
N/A Good |
Hot Working - Initial Forging |
N/A 2100 to 2300 ºF |
Annealing Temp. |
N/A 1850 to 2050 ºF |
Stress Relieving Temp. |
N/A 400 to 750 ºF |
Applications
|