Material |
N/A Type 316L Stainless Steel |
Shapeform |
N/A Welded Pipe |
O.D. |
N/A 2.375 inches60.325 mm |
I.P.S. Size |
N/A 2 inches |
Standard |
N/A Schedule 10 |
Wall Thickness |
N/A 0.180 inches4.572 mm |
Nominal I.D. |
N/A 12.390 inches314.706 mm |
Weight |
N/A 24.174 lbs/ft35.974876536 kg/m |
Condition |
N/A Cold Drawn Annealed Pickled |
Nominal Composition |
N/A 0.03% Max. Sulphur 0.045% Max. Phosphorus 0.08% Max. Carbon 1.00% Max. Silicon 10.0 to 14.0% Nickel 16% to 18% Chrome 2.0 to 3.0% Molybdenum 2.00% Max. Manganese |
ASTM Specification |
N/A ASTM A312 DUPont S.W. 41M MIL-P-144 UNS S31603 |
Random Length |
N/A 20 ft |
Steel Alloy Group |
N/A Austenitic |
Magnetic Properties |
N/A Non-Magnetic |
Harden By |
N/A Cold Work |
Corrosion Resistance |
N/A High |
Hardness |
N/A Low to Med. |
Strength |
N/A Low to Med. |
Ductility |
N/A High |
Toughness |
N/A High |
Elec. Conductance |
N/A Low |
Thermal Conductance |
N/A Low |
Thermal Expansion |
N/A High |
Heat Resistance (Scaling Strength) |
N/A High/High |
Yield Strength |
N/A 45000 lbs/in² |
Tensile Strength |
N/A 18200 lbs/in² |
Elongation percent in 2 inches |
N/A 50 % |
Hardness (Rockwell B) |
N/A 83 |
Creep Strength Load for 10000 Hr. with 1% Elongation at 1000°F |
N/A 25000 lbs/in² |
Creep Strength Load for 10000 Hr. with 1% Elongation at 1100°F |
N/A 7900 lbs/in² |
Creep Strength Load for 10000 Hr. with 1% Elongation at 1200°F |
N/A 7900 lbs/in² |
Creep Strength Load for 10000 Hr. with 1% Elongation at 1300°F |
N/A 7900 lbs/in² |
Density |
N/A 0.29 lbs/in³ |
Modulus of Elasticity in Tension |
N/A 29.0 x 106 lbs/in² |
Specific Heat (32 to 212°F) |
N/A 0.12 BTU/ºF/lbs |
Thermal Conductivity at 212°F |
N/A 9.04 BTU/hr.ft²/ft/ºF |
Thermal Conductivity at 932°F |
N/A 12.4 BTU/hr.ft²/ft/ºF |
Mean Coefficient of Thermal Expansion per °F (32 to 212°F) |
N/A 8.9 x 10-6 ºF |
Mean Coefficient of Thermal Expansion per °F (32 to 600°F) |
N/A 9.0 x 10-6 ºF |
Mean Coefficient of Thermal Expansion per °F (32 to 1000°F) |
N/A 9.7 x 10-6 ºF |
Mean Coefficient of Thermal Expansion per °F (32 to 1200°F) |
N/A 10.3 x 10-6 ºF |
Melting Point Range |
N/A 2500 to 2550 ºF |
Electrical Resistivity |
N/A 74 µΩ.cm |
Max. Operating Temp. (Continuous Service) |
N/A 1700 ºF |
Max. Operating Temp. (Intermittent Service) |
N/A 1600 ºF |
Welding Properties |
N/A Good |
Drawing and Stamping |
N/A Good |
Hot Working - Initial Forging |
N/A 2100 to 2300 ºF |
Annealing Temp. |
N/A 1950 to 2050 ºF |
Stress Relieving Temp. |
N/A 400 to 750 ºF |
|