| Material | Type 430 Stainless Steel | |||||||||
| Shapeform | Sheets | Coil | Sheets | Sheets | Coil | |||||
| Preparation | Paper Interleaved Vinyl Masked | |||||||||
| Thickness | 26 gauge | 26 gauge | 26 gauge | 26 gauge | 24 gauge | |||||
| Thickness | 0.0178 inches0.45212 mm | 0.0178 inches0.45212 mm | 0.0178 inches0.45212 mm | 0.0178 inches0.45212 mm | 0.0235 inches0.5969 mm | |||||
| Size | 30 x 120 | 36 x Coil | 36 x 96 | 36 x 120 | 36 x Coil | |||||
| Width | 30 | 36 | 36 | 36 | 36 | |||||
| Length | 120 | 96 | 120 | |||||||
| Sheet Weight per Unit Area | 0.742 lbs/ft²3.622444 kg/m² | 0.742 lbs/ft²3.622444 kg/m² | 0.742 lbs/ft²3.622444 kg/m² | 0.742 lbs/ft²3.622444 kg/m² | 0.989 lbs/ft²4.828298 kg/m² | |||||
| Estimated Weight per Sheet | 18.54 lbs8.39862 kg | 17.80 lbs8.0634 kg | 22.25 lbs10.07925 kg | |||||||
| Finish | No. 2B No. 2BA No. 3 No. 4 | |||||||||
| Condition | Bright Annealed Cold Rolled Annealed | |||||||||
| Nominal Composition | 0 or trace Nickel 0.06 to 0.35% Carbon 1.00% Max. Manganese 1.00% Max. Silicon 12% to 28% Chrome | |||||||||
| ASTM Specification | ASTM A240 ASTM A480 ASTM SA-240 UNS S43000 | |||||||||
| Steel Alloy Group | Ferritic | |||||||||
| Magnetic Properties | Magnetic | |||||||||
| Harden By | Cold Work | |||||||||
| Corrosion Resistance | Med. to High | |||||||||
| Hardness | Low | |||||||||
| Strength | Low | |||||||||
| Ductility | Med. | |||||||||
| Toughness | Low to Med. | |||||||||
| Elec. Conductance | Med. | |||||||||
| Thermal Conductance | Med. | |||||||||
| Thermal Expansion | Med. | |||||||||
| Heat Resistance (Scaling Strength) | High/Low | |||||||||
| Yield Strength | 50000 lbs/in² | |||||||||
| Tensile Strength | 74000 lbs/in² | |||||||||
| Elongation percent in 2 inches | 27 % | |||||||||
| Hardness (Rockwell B) | 85 | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1000°F | 8400 lbs/in² | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1100°F | 4900 lbs/in² | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1200°F | 2200 lbs/in² | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1300°F | 1400 lbs/in² | |||||||||
| Density | 0.28 lbs/in³ | |||||||||
| Modulus of Elasticity in Tension | 29.0 x 106 lbs/in² | |||||||||
| Specific Heat (32 to 212°F) | 0.11 BTU/ºF/lbs | |||||||||
| Thermal Conductivity at 212°F | 15.1 BTU/hr.ft²/ft/ºF | |||||||||
| Thermal Conductivity at 932°F | 15.2 BTU/hr.ft²/ft/ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 212°F) | 5.8 x 10-6 ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 600°F) | 6.1 x 10-6 ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 1000°F) | 6.3 x 10-6 ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 1200°F) | 6.6 x 10-6 ºF | |||||||||
| Melting Point Range | 2600 to 2750 ºF | |||||||||
| Electrical Resistivity | 60 µΩ.cm | |||||||||
| Max. Operating Temp. (Continuous Service) | 1550 ºF | |||||||||
| Max. Operating Temp. (Intermittent Service) | 1650 ºF | |||||||||
| Welding Properties | Fair-Limited ductility welds: some response to annealing | |||||||||
| Drawing and Stamping | Fair-Good | |||||||||
| Hot Working - Initial Forging | 2000 to 2200 ºF | |||||||||
| Annealing Temp. | 1500 to 1650 ºF | |||||||||
| Applications |
|
|||||||||
|
|
||||||||||