| Material | Type 301 Stainless Steel | |||||||||
| Shapeform | Coil & Strip | |||||||||
| Thickness | 0.035 inches0.8890 mm | 0.062 inches1.5748 mm | 0.093 inches2.3622 mm | 0.01 inches0.254 mm | 0.012 inches0.3048 mm | |||||
| Maximum Coil Width | 24 inches | |||||||||
| Strip Weight per Unit Area | 1.1693 lbs/ft²5.7085226 kg/m² | 2.5891 lbs/ft²12.6399862 kg/m² | 3.8837 lbs/ft²18.9602234 kg/m² | 0.4176 lbs/ft²2.0387232 kg/m² | 0.5011 lbs/ft²2.4463702 kg/m² | |||||
| Weight | 2.9232 lbs/ft4.35030624 kg/m | 5.17824 lbs/ft7.706256768 kg/m | 7.76736 lbs/ft11.559385152 kg/m | 0.8352 lbs/ft1.24294464 kg/m | 1.00224 lbs/ft1.491533568 kg/m | |||||
| Temper | Annealed | Annealed | Annealed | 1/4 Hard | 1/4 Hard | |||||
| Nominal Composition | 0.03% Max. Sulphur 0.045% Max. Phosphorus 0.10% Nitrogen 0.15% Max. Carbon 1.00% Max. Silicon 16.00 to 18.00% Chrominum 2.00% Max. Manganese 6.00 to 8.00% Nickel | |||||||||
| ASTM Specification | ASTM A240 ASTM A262 Prac E ASTM A480 ASTM A666 UNS S30100 | |||||||||
| Steel Alloy Group | Austenitic | |||||||||
| Magnetic Properties | Non-Magnetic | |||||||||
| Harden By | Cold Work | |||||||||
| Corrosion Resistance | High | |||||||||
| Hardness | Low to Med. | |||||||||
| Strength | Low to Med. | |||||||||
| Ductility | High | |||||||||
| Toughness | High | |||||||||
| Elec. Conductance | Low | |||||||||
| Thermal Conductance | Low | |||||||||
| Thermal Expansion | High | |||||||||
| Heat Resistance (Scaling Strength) | High/High | |||||||||
| Yield Strength | 43000 lbs/in² | 43000 lbs/in² | 43000 lbs/in² | 75000 lbs/in² | 75000 lbs/in² | |||||
| Tensile Strength | 106000 lbs/in² | 106000 lbs/in² | 106000 lbs/in² | 125000 lbs/in² | 125000 lbs/in² | |||||
| Elongation percent in 2 inches | 56 % | 56 % | 56 % | 25 % | 25 % | |||||
| Hardness (Rockwell B) | 86 | 86 | 86 | 25 | 25 | |||||
| Density | 0.29 lbs/in³ | |||||||||
| Modulus of Elasticity in Tension | 28.0 x 106 lbs/in² | |||||||||
| Specific Heat (32 to 212°F) | 0.12 BTU/ºF/lbs | |||||||||
| Thermal Conductivity at 212°F | 9.4 BTU/hr.ft²/ft/ºF | |||||||||
| Thermal Conductivity at 932°F | 12.4 BTU/hr.ft²/ft/ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 212°F) | 9.4 x 10-6 ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 600°F) | 9.5 x 10-6 ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 1000°F) | 10.1 x 10-6 ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 1200°F) | 10.4 x 10-6 ºF | |||||||||
| Melting Point Range | 2550 to 2590 ºF | |||||||||
| Electrical Resistivity | 69 µΩ.cm | |||||||||
| Max. Operating Temp. (Continuous Service) | 1600 ºF | |||||||||
| Max. Operating Temp. (Intermittent Service) | 1500 ºF | |||||||||
| Welding Properties | Very Good-Tough Welds | |||||||||
| Drawing and Stamping | Good | |||||||||
| Hot Working - Initial Forging | 2100 to 2300 ºF | |||||||||
| Annealing Temp. | 1850 to 2050 ºF | |||||||||
| Stress Relieving Temp. | 400 to 750 ºF | |||||||||
| Applications | Light drawing stretching, Forming, Good ductility | Light drawing stretching, Forming, Good ductility | ||||||||
| Applications |
|
|||||||||
|
|
||||||||||