Cold Rolled, Annealed No. 2B Finish

Can also be furnished:
No. 3 Finish - Polished One or Two Sides
No. 4 Finish - Polished One or Two Sides
Bright Annealed, rolled-on and other finishes available on application.
Non-Magnetic (May be Slightly magnetic when cold worked)

Paper Interleaved or Vinyl Masked:
22 Gauge And Heavier
A.S.T.M. A262 Prac E A.S.T.M. A240/A480 ASME SA-240 AMS 5513
Unit of Measure

Specifications

Material

Type 304 Stainless Steel

Shapeform

Sheets

Preparation

Paper Interleaved Vinyl Masked

Thickness

22 gauge

Thickness

0.0291 inches0.73914 mm

Size

36 x 96

Width

36

Length

96

Sheet Weight per Unit Area

1.260 lbs/ft²6.15132 kg/m²

Estimated Weight per Sheet

30.24 lbs13.69872 kg

Finish

No. 2B No. 3 No. 4

Condition

Bright Annealed Cold Rolled Annealed

Nominal Composition

0 to 0.25% Carbon 1.00% Max. Silicon 2.00% Max. Manganese 6 to 36% Nickel 7 to 30% Chrome

ASTM Specification

AMS 513 ASTM A240 ASTM A262 Prac E ASTM A480 ASTM SA-240 UNS S30400

Typical Mechanical Properties

Steel Alloy Group

Austenitic

Magnetic Properties

Non-Magnetic

Harden By

Cold Work

Corrosion Resistance

High

Hardness

Low to Med.

Strength

Low to Med.

Ductility

High

Toughness

High

Elec. Conductance

Low

Thermal Conductance

Low

Thermal Expansion

High

Heat Resistance (Scaling Strength)

High/High

Comparative Characteristics and Applications

Yield Strength

46000 lbs/in²

Tensile Strength

89000 lbs/in²

Elongation percent in 2 inches

55 %

Hardness (Rockwell B)

86

Creep Strength Load for 10000 Hr. with 1% Elongation at 1000°F

17000 lbs/in²

Creep Strength Load for 10000 Hr. with 1% Elongation at 1100°F

12000 lbs/in²

Creep Strength Load for 10000 Hr. with 1% Elongation at 1200°F

7000 lbs/in²

Creep Strength Load for 10000 Hr. with 1% Elongation at 1300°F

4000 lbs/in²

Density

0.29 lbs/in³

Modulus of Elasticity in Tension

28.0 x 106 lbs/in²

Specific Heat (32 to 212°F)

0.12 BTU/ºF/lbs

Thermal Conductivity at 212°F

9.4 BTU/hr.ft²/ft/ºF

Thermal Conductivity at 932°F

12.4 BTU/hr.ft²/ft/ºF

Mean Coefficient of Thermal Expansion per °F (32 to 212°F)

9.6 x 10-6 ºF

Mean Coefficient of Thermal Expansion per °F (32 to 600°F)

9.9 x 10-6 ºF

Mean Coefficient of Thermal Expansion per °F (32 to 1000°F)

10.2 x 10-6 ºF

Mean Coefficient of Thermal Expansion per °F (32 to 1200°F)

10.4 x 10-6 ºF

Melting Point Range

2550 to 2650 ºF

Electrical Resistivity

72 µΩ.cm

Max. Operating Temp. (Continuous Service)

1650 ºF

Max. Operating Temp. (Intermittent Service)

1500 ºF

Welding Properties

Very Good-Tough Welds

Drawing and Stamping

Very Good

Hot Working - Initial Forging

2100 to 2300 ºF

Annealing Temp.

1850 to 2050 ºF

Stress Relieving Temp.

400 to 750 ºF

Applications

N/A

  • Rapid transit cars, buses, aircraft, cargo containers
  • Retractor springs
  • Hose clamps
  • Conveyors
  • Bottling machinery
  • Jewelry
  • Cryogenic vessels and components
  • Still tubes
  • Expand metal parts
  • Mixing bowls
  • Dryers
  • Furnace parts
  • Heat exchangers
  • Paper mill equipment
  • Oil refining equipment
  • Textile industry
  • Dyeing equipment
  • Jet engine parts
  • Welded storage tanks for organic chemicals
  • Combustion chambers
  • Furnace arch supports
  • Kiln linings
  • Smoke control ductwork
  • Coal chutes
  • Gauge parts
  • Cutlery
  • Fish hooks
  • Glass molds
  • Bank vaults
  • Fasteners
  • Skewers
  • Dairy industry
  • Burner and emission control components
  • Recuperators
  • Pipes, tubes