Yield Strength
|
|
50000 lbs/in²
|
|
|
|
Tensile Strength
|
|
74000 lbs/in²
|
|
|
|
Elongation percent in 2 inches
|
|
27 %
|
|
|
|
Hardness (Rockwell B)
|
|
85
|
|
|
|
Creep Strength Load for 10000 Hr. with 1% Elongation at 1000°F
|
|
8400 lbs/in²
|
|
|
|
Creep Strength Load for 10000 Hr. with 1% Elongation at 1100°F
|
|
4900 lbs/in²
|
|
|
|
Creep Strength Load for 10000 Hr. with 1% Elongation at 1200°F
|
|
2200 lbs/in²
|
|
|
|
Creep Strength Load for 10000 Hr. with 1% Elongation at 1300°F
|
|
1400 lbs/in²
|
|
|
|
Density
|
|
0.28 lbs/in³
|
|
|
|
Modulus of Elasticity in Tension
|
|
29.0 x 106 lbs/in²
|
|
|
|
Specific Heat (32 to 212°F)
|
|
0.11 BTU/ºF/lbs
|
|
|
|
Thermal Conductivity at 212°F
|
|
15.1 BTU/hr.ft²/ft/ºF
|
|
|
|
Thermal Conductivity at 932°F
|
|
15.2 BTU/hr.ft²/ft/ºF
|
|
|
|
Mean Coefficient of Thermal Expansion per °F (32 to 212°F)
|
|
5.8 x 10-6 ºF
|
|
|
|
Mean Coefficient of Thermal Expansion per °F (32 to 600°F)
|
|
6.1 x 10-6 ºF
|
|
|
|
Mean Coefficient of Thermal Expansion per °F (32 to 1000°F)
|
|
6.3 x 10-6 ºF
|
|
|
|
Mean Coefficient of Thermal Expansion per °F (32 to 1200°F)
|
|
6.6 x 10-6 ºF
|
|
|
|
Melting Point Range
|
|
2600 to 2750 ºF
|
|
|
|
Electrical Resistivity
|
|
60 µΩ.cm
|
|
|
|
Max. Operating Temp. (Continuous Service)
|
|
1550 ºF
|
|
|
|
Max. Operating Temp. (Intermittent Service)
|
|
1650 ºF
|
|
|
|
Welding Properties
|
|
Fair-Limited ductility welds: some response to annealing
|
|
|
|
Drawing and Stamping
|
|
Fair-Good
|
|
|
|
Hot Working - Initial Forging
|
|
2000 to 2200 ºF
|
|
|
|
Annealing Temp.
|
|
1500 to 1650 ºF
|
|
|