Material |
N/A Type 316L Stainless Steel |
Shapeform |
N/A Plates |
Thickness |
N/A 1/2 inches |
Thickness |
N/A 0.500 inches12.7 mm |
Size |
N/A 60 x 240 |
Width |
N/A 60 |
Length |
N/A 240 |
Weight per Plate |
N/A 2166 lbs981.198 kg |
Finish |
N/A No. 2D |
Condition |
N/A Hot Rolled Annealed Pickled |
Nominal Composition |
N/A 0 to 0.25% Carbon 1.00% Max. Silicon 2.00% Max. Manganese 6 to 36% Nickel 7 to 30% Chrome |
ASTM Specification |
N/A ASTM A240 ASTM A262 Prac E ASTM A480 ASTM SA-240 UNS S31603 |
Steel Alloy Group |
N/A Austenitic |
Magnetic Properties |
N/A Non-Magnetic |
Harden By |
N/A Cold Work |
Corrosion Resistance |
N/A High |
Hardness |
N/A Low to Med. |
Strength |
N/A Low to Med. |
Ductility |
N/A High |
Toughness |
N/A High |
Elec. Conductance |
N/A Low |
Thermal Conductance |
N/A Low |
Thermal Expansion |
N/A High |
Heat Resistance (Scaling Strength) |
N/A High/High |
Yield Strength |
N/A 40000 lbs/in² |
Tensile Strength |
N/A 84000 lbs/in² |
Elongation percent in 2 inches |
N/A 52 % |
Hardness (Rockwell B) |
N/A 81 |
Creep Strength Load for 10000 Hr. with 1% Elongation at 1000°F |
N/A 25000 lbs/in² |
Creep Strength Load for 10000 Hr. with 1% Elongation at 1100°F |
N/A 7900 lbs/in² |
Creep Strength Load for 10000 Hr. with 1% Elongation at 1200°F |
N/A 7900 lbs/in² |
Creep Strength Load for 10000 Hr. with 1% Elongation at 1300°F |
N/A 7900 lbs/in² |
Density |
N/A 0.29 lbs/in³ |
Modulus of Elasticity in Tension |
N/A 29.0 x 106 lbs/in² |
Specific Heat (32 to 212°F) |
N/A 0.12 BTU/ºF/lbs |
Thermal Conductivity at 212°F |
N/A 9.04 BTU/hr.ft²/ft/ºF |
Thermal Conductivity at 932°F |
N/A 12.4 BTU/hr.ft²/ft/ºF |
Mean Coefficient of Thermal Expansion per °F (32 to 212°F) |
N/A 8.8 x 10-6 ºF |
Mean Coefficient of Thermal Expansion per °F (32 to 600°F) |
N/A 9.0 x 10-6 ºF |
Mean Coefficient of Thermal Expansion per °F (32 to 1000°F) |
N/A 9.7 x 10-6 ºF |
Mean Coefficient of Thermal Expansion per °F (32 to 1200°F) |
N/A 10.3 x 10-6 ºF |
Melting Point Range |
N/A 2500 to 2550 ºF |
Electrical Resistivity |
N/A 74 µΩ.cm |
Max. Operating Temp. (Continuous Service) |
N/A 1700 ºF |
Max. Operating Temp. (Intermittent Service) |
N/A 1600 ºF |
Welding Properties |
N/A Good |
Drawing and Stamping |
N/A Good |
Hot Working - Initial Forging |
N/A 2100 to 2300 ºF |
Annealing Temp. |
N/A 1950 to 2050 ºF |
Stress Relieving Temp. |
N/A 400 to 750 ºF |
N/A
|