All Categories > Nickel and High Temperature Alloys > Inconel® > Inconel® 617 Plate > Item # I617-2500  


Item # I617-2500, Inconel® 617 Plate

Inconel 617 is a nickel-chromium-cobalt-molybdenum alloy with an exceptional combination of metallurgical stability, strength and oxidation resistance at high temperatures. Resistance to oxidation is enhanced by an aluminum addition. Inconel 617 also resists a wide range of corrosive aqueous environments. Inconel 617 is used in gas turbines for combustion cans, ducting and transition liners; for petrochemical processing; for heat-treating equipment; and in nitric acid production. Standard product forms are round, forging stock, extruded section, plate, sheet, strip, pipe, tube and wire.





Specifications  · Nickel Alloy Compositions  · Typical Mechanical Properties

Specifications

Material
Inconel®

Shapeform
Plates

Thickness
2 1/2 inches

Thickness
2.500 inches

Plate Weight per Unit Area
0.79323 lbs/in²


Nickel Alloy Compositions

Alloy
Inconel® 617

Basic Composition
1.2% Aluminum
1.5% Iron
125% Cobalt
22.0% Chrominum
52.0% Nickel
9.0% Molybdenum

Density
0.302 lbs/in³

ASTM Specification
ASME SB-166(w)
ASTM B166(w)
SAE 5887
UNS N06617


Typical Mechanical Properties

Melting Temperature Range
2430 to 2510 ºF
1330 to 1380 ºC

Rupture Strength (1000 h at 1200°F/650°C)
47000 psi
320 MPa

Rupture Strength (1000 h at 1400°F/760°C)
22000 psi
150 MPa

Rupture Strength (1000 h at 1600°F/870°C)
8400 psi
58 MPa

Rupture Strength (1000 h at 1800°F/980°C)
3600 psi
25 MPa

Rupture Strength (1000 h at 2000°F/1095°C)
1500 psi
10 MPa