| Items |
 304-405-068WP Stainless Steel Welded Pipe - Type 304 |
304-405-095WP Stainless Steel Welded Pipe - Type 304 |
304-540-088WP Stainless Steel Welded Pipe - Type 304 |
304-540-119WP Stainless Steel Welded Pipe - Type 304 |
304-675-091WP Stainless Steel Welded Pipe - Type 304 |
|||||
| Material | Type 304 Stainless Steel | |||||||||
| Shapeform | Welded Pipe | |||||||||
| O.D. | 0.405 inches10.287 mm | 0.405 inches10.287 mm | 0.54 inches13.716 mm | 0.54 inches13.716 mm | 0.675 inches17.145 mm | |||||
| I.P.S. Size | 1/8 inches | 1/8 inches | 1/4 inches | 1/4 inches | 3/8 inches | |||||
| Standard | Schedule 40 | Schedule 80 | Schedule 40 | Schedule 80 | Schedule 40 | |||||
| Wall Thickness | 0.068 inches1.7272 mm | 0.095 inches2.4130 mm | 0.088 inches2.2352 mm | 0.119 inches3.0226 mm | 0.091 inches2.3114 mm | |||||
| Nominal I.D. | 0.269 inches6.8326 mm | 0.215 inches5.461 mm | 0.364 inches9.2456 mm | 0.302 inches7.6708 mm | 0.493 inches12.5222 mm | |||||
| Weight | 0.2448 lbs/ft0.3643025472 kg/m | 0.3146 lbs/ft0.4681763944 kg/m | 0.425 lbs/ft0.6324697 kg/m | 0.5353 lbs/ft0.7966141892 kg/m | 0.5678 lbs/ft0.8449795192 kg/m | |||||
| Condition | Cold Drawn Annealed Pickled | |||||||||
| Nominal Composition | 0.03% Max. Sulphur 0.045% Max. Phosphorus 0.08% Max. Carbon 1.00% Max. Silicon 18 to 20% Chrome 2.00% Max. Manganese 8.0% to 12.0% Nickel | |||||||||
| ASTM Specification | ASTM A312 DUPont S.W. 41M MIL-P-144 UNS S30400 | |||||||||
| Random Length | 20 ft | |||||||||
| Steel Alloy Group | Austenitic | |||||||||
| Magnetic Properties | Non-Magnetic | |||||||||
| Harden By | Cold Work | |||||||||
| Corrosion Resistance | High | |||||||||
| Hardness | Low to Med. | |||||||||
| Strength | Low to Med. | |||||||||
| Ductility | High | |||||||||
| Toughness | High | |||||||||
| Elec. Conductance | Low | |||||||||
| Thermal Conductance | Low | |||||||||
| Thermal Expansion | High | |||||||||
| Heat Resistance (Scaling Strength) | High/High | |||||||||
| Yield Strength | 46000 lbs/in² | |||||||||
| Tensile Strength | 89000 lbs/in² | |||||||||
| Elongation percent in 2 inches | 55 % | |||||||||
| Hardness (Rockwell B) | 86 | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1000°F | 17000 lbs/in² | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1100°F | 12000 lbs/in² | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1200°F | 7000 lbs/in² | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1300°F | 4000 lbs/in² | |||||||||
| Density | 0.29 lbs/in³ | |||||||||
| Modulus of Elasticity in Tension | 28.0 x 106 lbs/in² | |||||||||
| Specific Heat (32 to 212°F) | 0.12 BTU/ºF/lbs | |||||||||
| Thermal Conductivity at 212°F | 9.4 BTU/hr.ft²/ft/ºF | |||||||||
| Thermal Conductivity at 932°F | 12.4 BTU/hr.ft²/ft/ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 212°F) | 9.6 x 10-6 ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 600°F) | 9.9 x 10-6 ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 1000°F) | 10.2 x 10-6 ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 1200°F) | 10.4 x 10-6 ºF | |||||||||
| Melting Point Range | 2550 to 2650 ºF | |||||||||
| Electrical Resistivity | 72 µΩ.cm | |||||||||
| Max. Operating Temp. (Continuous Service) | 1650 ºF | |||||||||
| Max. Operating Temp. (Intermittent Service) | 1500 ºF | |||||||||
| Welding Properties | Very Good-Tough Welds | |||||||||
| Drawing and Stamping | Very Good | |||||||||
| Hot Working - Initial Forging | 2100 to 2300 ºF | |||||||||
| Annealing Temp. | 1850 to 2050 ºF | |||||||||
| Stress Relieving Temp. | 400 to 750 ºF | |||||||||
| Applications |
|
|||||||||
|
|
||||||||||