Material | N/A Type 316 Stainless Steel | |||||||||
Shapeform | N/A Round Bar | |||||||||
Diameter | N/A 1/16 inches | N/A 3/32 inches | N/A 1/8 inches | N/A 5/32 inches | N/A 3/16 inches | |||||
Diameter | N/A 0.0625 inches1.5875 mm | N/A 0.0938 inches2.38252 mm | N/A 0.125 inches3.175 mm | N/A 0.1563 inches3.97002 mm | N/A 0.1875 inches4.7625 mm | |||||
Weight | N/A 0.010 lbs/ft0.01488 kg/m | N/A 0.0240 lbs/ft0.035712 kg/m | N/A 0.042 lbs/ft0.062496 kg/m | N/A 0.065 lbs/ft0.09672 kg/m | N/A 0.094 lbs/ft0.139872 kg/m | |||||
Finish | N/A No. 2B | |||||||||
Condition | N/A Cold Finished Annealed | |||||||||
Nominal Composition | N/A 0 to 0.25% Carbon 1.00% Max. Silicon 2.00% Max. Manganese 6 to 36% Nickel 7 to 30% Chrome | |||||||||
ASTM Specification | N/A ASTM A276 UNS S31600 | |||||||||
Steel Alloy Group | N/A Austenitic | |||||||||
Magnetic Properties | N/A Non-Magnetic | |||||||||
Harden By | N/A Cold Work | |||||||||
Corrosion Resistance | N/A High | |||||||||
Hardness | N/A Low to Med. | |||||||||
Strength | N/A Low to Med. | |||||||||
Ductility | N/A High | |||||||||
Toughness | N/A High | |||||||||
Elec. Conductance | N/A Low | |||||||||
Thermal Conductance | N/A Low | |||||||||
Thermal Expansion | N/A High | |||||||||
Heat Resistance (Scaling Strength) | N/A High/High | |||||||||
Yield Strength | N/A 45000 lbs/in² | |||||||||
Tensile Strength | N/A 18200 lbs/in² | |||||||||
Elongation percent in 2 inches | N/A 50 % | |||||||||
Hardness (Rockwell B) | N/A 83 | |||||||||
Creep Strength Load for 10000 Hr. with 1% Elongation at 1000°F | N/A 25000 lbs/in² | |||||||||
Creep Strength Load for 10000 Hr. with 1% Elongation at 1100°F | N/A 18200 lbs/in² | |||||||||
Creep Strength Load for 10000 Hr. with 1% Elongation at 1200°F | N/A 12700 lbs/in² | |||||||||
Creep Strength Load for 10000 Hr. with 1% Elongation at 1300°F | N/A 7900 lbs/in² | |||||||||
Density | N/A 0.29 lbs/in³ | |||||||||
Modulus of Elasticity in Tension | N/A 29.0 x 106 lbs/in² | |||||||||
Specific Heat (32 to 212°F) | N/A 0.12 BTU/ºF/lbs | |||||||||
Thermal Conductivity at 212°F | N/A 9.4 BTU/hr.ft²/ft/ºF | |||||||||
Thermal Conductivity at 932°F | N/A 12.4 BTU/hr.ft²/ft/ºF | |||||||||
Mean Coefficient of Thermal Expansion per °F (32 to 212°F) | N/A 8.8 x 10-6 ºF | |||||||||
Mean Coefficient of Thermal Expansion per °F (32 to 600°F) | N/A 9.0 x 10-6 ºF | |||||||||
Mean Coefficient of Thermal Expansion per °F (32 to 1000°F) | N/A 9.7 x 10-6 ºF | |||||||||
Mean Coefficient of Thermal Expansion per °F (32 to 1200°F) | N/A 10.3 x 10-6 ºF | |||||||||
Melting Point Range | N/A 2500 to 2550 ºF | |||||||||
Electrical Resistivity | N/A 74 µΩ.cm | |||||||||
Max. Operating Temp. (Continuous Service) | N/A 1650 ºF | |||||||||
Max. Operating Temp. (Intermittent Service) | N/A 1500 ºF | |||||||||
Welding Properties | N/A Very Good-Tough Welds | |||||||||
Drawing and Stamping | N/A Good | |||||||||
Hot Working - Initial Forging | N/A 2100 to 2300 ºF | |||||||||
Annealing Temp. | N/A 1850 to 2050 ºF | |||||||||
Stress Relieving Temp. | N/A 400 to 750 ºF | |||||||||