| Items |
 I617-1875 Inconel® 617 Plate |
I617-250 Inconel® 617 Plate |
I617-375 Inconel® 617 Plate |
I617-500 Inconel® 617 Plate |
I617-625 Inconel® 617 Plate |
|||||
| Material | Inconel® | |||||||||
| Shapeform | Plates | |||||||||
| Thickness | 3/16 inches | 1/4 inches | 3/8 inches | 1/2 inches | 5/8 inches | |||||
| Thickness | 0.1875 inches4.75 mm | 0.25 inches6.3500 mm | 0.375 inches9.52 mm | 0.500 inches12.7 mm | 0.625 inches15.87 mm | |||||
| Plate Weight per Unit Area | 0.06315 lbs/in²44.39884524 kg/m² | 0.08317 lbs/in²58.474298632 kg/m² | 0.12245 lbs/in²86.09087252 kg/m² | 0.16018 lbs/in²112.617688528 kg/m² | 0.20023 lbs/in²140.775626008 kg/m² | |||||
| Alloy | Inconel® 617 | |||||||||
| Basic Composition | 1.2% Aluminum 1.5% Iron 125% Cobalt 22.0% Chrominum 52.0% Nickel 9.0% Molybdenum | |||||||||
| Density | 0.302 lbs/in³8.36 g/cm³ | |||||||||
| ASTM Specification | ASME SB-166(w) ASTM B166(w) SAE 5887 UNS N06617 | |||||||||
| Melting Temperature Range | 2430 to 2510 ºF1330 to 1380 ºC | |||||||||
| Rupture Strength (1000 h at 1200°F/650°C) | 47000 psi320 MPa | |||||||||
| Rupture Strength (1000 h at 1400°F/760°C) | 22000 psi150 MPa | |||||||||
| Rupture Strength (1000 h at 1600°F/870°C) | 8400 psi58 MPa | |||||||||
| Rupture Strength (1000 h at 1800°F/980°C) | 3600 psi25 MPa | |||||||||
| Rupture Strength (1000 h at 2000°F/1095°C) | 1500 psi10 MPa | |||||||||
|
|
||||||||||