Incoloy 800HT is a nickel-iron-chromium alloy with good strength and excellent resistance to oxidation and carburization in high-temperature atmospheres. It also resists corrosion by many aqueous environments. Incoloy 800HT maintains a stable, austenitic structure during prolonged exposure to high temperatures. Incoloy 800HT is used for process piping, heat exchangers, carburizing equipment, heating-element sheathing and nuclear steam-generator tubing. Standard product forms are round, flats, forging stock, pipe, tube, plate, sheet, strip and wire.
Nickel & High Temperature Alloy Sheets
Unit of Measure
Items Nickel & High Temperature Alloy Sheets
I800HT-025
Incoloy® 800HT Sheet
Nickel & High Temperature Alloy Sheets
I800HT-060
Incoloy® 800HT Sheet
Nickel & High Temperature Alloy Sheets
I800HT-062
Incoloy® 800HT Sheet
Nickel & High Temperature Alloy Sheets
I800HT-093
Incoloy® 800HT Sheet
Nickel & High Temperature Alloy Sheets
I800HT-104
Incoloy® 800HT Sheet
Material N/A Incoloy®
Shapeform N/A Sheets
Thickness N/A 0.025 inches0.6350 mm N/A 0.060 inches1.524 mm N/A 0.062 inches1.5748 mm N/A 0.093 inches2.3622 mm N/A 0.104 inches2.6416 mm
Alloy N/A Incoloy 800HT
Basic Composition N/A 0.015% Max. Sulphur 0.10% Carbon 0.60% Aluminum 0.60% Titanium 0.75% Max. Copper 1.0% Max. Silicon 1.20% Aluminum +Titanium 1.50% Max. Manganese 23.0% Chrominum 35.0% Nickel 39.5% Min. Iron
Density N/A 0.287 lbs/in³7.94 g/cm³
ASTM Specification N/A ASME SB-409 ASTM B409 UNS N08811
Melting Temperature Range N/A 2475 to 2525 ºF1357 to 1385 ºC
Rupture Strength (1000 h at 1200°F/650°C) N/A 24000 psi165 MPa
Rupture Strength (1000 h at 1300°F/705°C) N/A 15000 psi105 MPa
Rupture Strength (1000 h at 1400°F/760°C) N/A 10000 psi70 MPa
Rupture Strength (1000 h at 1600°F/870°C) N/A 4700 psi32 MPa
Rupture Strength (1000 h at 1800°F/980°C) N/A 2000 psi14 MPa