| Items |
 I800HT-1875 Incoloy® 800HT Plate |
I800HT-250 Incoloy® 800HT Plate |
I800HT-3125 Incoloy® 800HT Plate |
I800HT-375 Incoloy® 800HT Plate |
I800HT-500 Incoloy® 800HT Plate |
|||||
| Material | Incoloy® | |||||||||
| Shapeform | Plates | |||||||||
| Thickness | 3/16 inches | 1/4 inches | 5/16 inches | 3/8 inches | 1/2 inches | |||||
| Thickness | 0.1875 inches4.75 mm | 0.25 inches6.3500 mm | 0.3125 inches7.92 mm | 0.375 inches9.52 mm | 0.500 inches12.7 mm | |||||
| Plate Weight per Unit Area | 0.06000 lbs/in²42.184176 kg/m² | 0.07900 lbs/in²55.5424984 kg/m² | 0.09700 lbs/in²68.1977512 kg/m² | 0.1169 lbs/in²82.18883624 kg/m² | 0.15350 lbs/in²107.9211836 kg/m² | |||||
| Alloy | Incoloy 800HT | |||||||||
| Basic Composition | 0.015% Max. Sulphur 0.10% Carbon 0.60% Aluminum 0.60% Titanium 0.75% Max. Copper 1.0% Max. Silicon 1.20% Aluminum +Titanium 1.50% Max. Manganese 23.0% Chrominum 35.0% Nickel 39.5% Min. Iron | |||||||||
| Density | 0.287 lbs/in³7.94 g/cm³ | |||||||||
| ASTM Specification | ASME SB-409 ASTM B409 UNS N08811 | |||||||||
| Melting Temperature Range | 2475 to 2525 ºF1357 to 1385 ºC | |||||||||
| Rupture Strength (1000 h at 1200°F/650°C) | 24000 psi165 MPa | |||||||||
| Rupture Strength (1000 h at 1300°F/705°C) | 15000 psi105 MPa | |||||||||
| Rupture Strength (1000 h at 1400°F/760°C) | 10000 psi70 MPa | |||||||||
| Rupture Strength (1000 h at 1600°F/870°C) | 4700 psi32 MPa | |||||||||
| Rupture Strength (1000 h at 1800°F/980°C) | 2000 psi14 MPa | |||||||||
|
|
||||||||||