| Items |
 304-28-36-96 Stainless Steel Sheet - Type 304 |
304-28-36-120 Stainless Steel Sheet - Type 304 |
304-26-36-96 Stainless Steel Sheet - Type 304 |
304-26-36-120 Stainless Steel Sheet - Type 304 |
304-26-48-96 Stainless Steel Sheet - Type 304 |
|||||
| Material | Type 304 Stainless Steel | |||||||||
| Shapeform | Sheets | |||||||||
| Preparation | Paper Interleaved Vinyl Masked | |||||||||
| Thickness | 28 gauge | 28 gauge | 26 gauge | 26 gauge | 26 gauge | |||||
| Thickness | 0.015 inches0.381 mm | 0.015 inches0.381 mm | 0.0178 inches0.45212 mm | 0.0178 inches0.45212 mm | 0.0178 inches0.45212 mm | |||||
| Size | 36 x 96 | 36 x 120 | 36 x 96 | 36 x 120 | 48 x 96 | |||||
| Width | 36 | 36 | 36 | 36 | 48 | |||||
| Length | 96 | 120 | 96 | 120 | 96 | |||||
| Sheet Weight per Unit Area | 0.630 lbs/ft²3.07566 kg/m² | 0.630 lbs/ft²3.07566 kg/m² | 0.756 lbs/ft²3.690792 kg/m² | 0.756 lbs/ft²3.690792 kg/m² | 0.756 lbs/ft²3.690792 kg/m² | |||||
| Estimated Weight per Sheet | 15.12 lbs6.84936 kg | 18.90 lbs8.5617 kg | 18.15 lbs8.22195 kg | 22.68 lbs10.27404 kg | 24.19 lbs10.95807 kg | |||||
| Finish | No. 2B No. 3 No. 4 | |||||||||
| Condition | Bright Annealed Cold Rolled Annealed | |||||||||
| Nominal Composition | 0 to 0.25% Carbon 1.00% Max. Silicon 2.00% Max. Manganese 6 to 36% Nickel 7 to 30% Chrome | |||||||||
| ASTM Specification | AMS 513 ASTM A240 ASTM A262 Prac E ASTM A480 ASTM SA-240 UNS S30400 | |||||||||
| Steel Alloy Group | Austenitic | |||||||||
| Magnetic Properties | Non-Magnetic | |||||||||
| Harden By | Cold Work | |||||||||
| Corrosion Resistance | High | |||||||||
| Hardness | Low to Med. | |||||||||
| Strength | Low to Med. | |||||||||
| Ductility | High | |||||||||
| Toughness | High | |||||||||
| Elec. Conductance | Low | |||||||||
| Thermal Conductance | Low | |||||||||
| Thermal Expansion | High | |||||||||
| Heat Resistance (Scaling Strength) | High/High | |||||||||
| Yield Strength | 46000 lbs/in² | |||||||||
| Tensile Strength | 89000 lbs/in² | |||||||||
| Elongation percent in 2 inches | 55 % | |||||||||
| Hardness (Rockwell B) | 86 | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1000°F | 17000 lbs/in² | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1100°F | 12000 lbs/in² | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1200°F | 7000 lbs/in² | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1300°F | 4000 lbs/in² | |||||||||
| Density | 0.29 lbs/in³ | |||||||||
| Modulus of Elasticity in Tension | 28.0 x 106 lbs/in² | |||||||||
| Specific Heat (32 to 212°F) | 0.12 BTU/ºF/lbs | |||||||||
| Thermal Conductivity at 212°F | 9.4 BTU/hr.ft²/ft/ºF | |||||||||
| Thermal Conductivity at 932°F | 12.4 BTU/hr.ft²/ft/ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 212°F) | 9.6 x 10-6 ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 600°F) | 9.9 x 10-6 ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 1000°F) | 10.2 x 10-6 ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 1200°F) | 10.4 x 10-6 ºF | |||||||||
| Melting Point Range | 2550 to 2650 ºF | |||||||||
| Electrical Resistivity | 72 µΩ.cm | |||||||||
| Max. Operating Temp. (Continuous Service) | 1650 ºF | |||||||||
| Max. Operating Temp. (Intermittent Service) | 1500 ºF | |||||||||
| Welding Properties | Very Good-Tough Welds | |||||||||
| Drawing and Stamping | Very Good | |||||||||
| Hot Working - Initial Forging | 2100 to 2300 ºF | |||||||||
| Annealing Temp. | 1850 to 2050 ºF | |||||||||
| Stress Relieving Temp. | 400 to 750 ºF | |||||||||
| Applications |
|
|||||||||
|
|
||||||||||