| Items |
 316-540-088SP Stainless Steel Seamless Pipe - Type 316 |
316-540-119SP Stainless Steel Seamless Pipe - Type 316 |
316-840-109SP Stainless Steel Seamless Pipe - Type 316 |
316-840-147SP Stainless Steel Seamless Pipe - Type 316 |
316-1050-113SP Stainless Steel Seamless Pipe - Type 316 |
|||||
| Material | Type 316 Stainless Steel | |||||||||
| Shapeform | Seamless Pipe | |||||||||
| O.D. | 0.54 inches13.716 mm | 0.54 inches13.716 mm | 0.84 inches21.336 mm | 0.84 inches21.336 mm | 1.05 inches26.67 mm | |||||
| I.P.S. Size | 1/4 inches | 1/4 inches | 1/2 inches | 1/2 inches | 3/4 inches | |||||
| Standard | Schedule 40 | Schedule 80 | Schedule 40 | Schedule 80 | Schedule 40 | |||||
| Wall Thickness | 0.088 inches2.2352 mm | 0.119 inches3.0226 mm | 0.109 inches2.7686 mm | 0.147 inches3.7338 mm | 0.113 inches2.8702 mm | |||||
| Nominal I.D. | 0.364 inches9.2456 mm | 0.302 inches7.6708 mm | 0.622 inches15.7988 mm | 0.546 inches13.8684 mm | 0.824 inches20.9296 mm | |||||
| Weight | 0.425 lbs/ft0.6324697 kg/m | 0.5353 lbs/ft0.7966141892 kg/m | 0.8513 lbs/ft1.2668740132 kg/m | 1.088 lbs/ft1.619122432 kg/m | 1.131 lbs/ft1.683113484 kg/m | |||||
| Condition | Cold Drawn Annealed Pickled | |||||||||
| Nominal Composition | 0.03% Max. Sulphur 0.045% Max. Phosphorus 0.08% Max. Carbon 1.00% Max. Silicon 10.0 to 14.0% Nickel 16% to 18% Chrome 2.0 to 3.0% Molybdenum 2.00% Max. Manganese | |||||||||
| ASTM Specification | ASTM A312 MIL-P-144 UNS S31600 | |||||||||
| Random Length | 20 ft | |||||||||
| Steel Alloy Group | Austenitic | |||||||||
| Magnetic Properties | Non-Magnetic | |||||||||
| Harden By | Cold Work | |||||||||
| Corrosion Resistance | High | |||||||||
| Hardness | Low to Med. | |||||||||
| Strength | Low to Med. | |||||||||
| Ductility | High | |||||||||
| Toughness | High | |||||||||
| Elec. Conductance | Low | |||||||||
| Thermal Conductance | Low | |||||||||
| Thermal Expansion | High | |||||||||
| Heat Resistance (Scaling Strength) | High/High | |||||||||
| Yield Strength | 45000 lbs/in² | |||||||||
| Tensile Strength | 18200 lbs/in² | |||||||||
| Elongation percent in 2 inches | 50 % | |||||||||
| Hardness (Rockwell B) | 83 | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1000°F | 25000 lbs/in² | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1100°F | 18200 lbs/in² | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1200°F | 12700 lbs/in² | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1300°F | 7900 lbs/in² | |||||||||
| Density | 0.29 lbs/in³ | |||||||||
| Modulus of Elasticity in Tension | 29.0 x 106 lbs/in² | |||||||||
| Specific Heat (32 to 212°F) | 0.12 BTU/ºF/lbs | |||||||||
| Thermal Conductivity at 212°F | 9.4 BTU/hr.ft²/ft/ºF | |||||||||
| Thermal Conductivity at 932°F | 12.4 BTU/hr.ft²/ft/ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 212°F) | 8.8 x 10-6 ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 600°F) | 9.0 x 10-6 ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 1000°F) | 9.7 x 10-6 ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 1200°F) | 10.3 x 10-6 ºF | |||||||||
| Melting Point Range | 2500 to 2550 ºF | |||||||||
| Electrical Resistivity | 74 µΩ.cm | |||||||||
| Max. Operating Temp. (Continuous Service) | 1650 ºF | |||||||||
| Max. Operating Temp. (Intermittent Service) | 1500 ºF | |||||||||
| Welding Properties | Very Good-Tough Welds | |||||||||
| Drawing and Stamping | Good | |||||||||
| Hot Working - Initial Forging | 2100 to 2300 ºF | |||||||||
| Annealing Temp. | 1850 to 2050 ºF | |||||||||
| Stress Relieving Temp. | 400 to 750 ºF | |||||||||
| Applications |
|
|||||||||
|
|
||||||||||