| Items |
 /Asset/Bars2.jpg 410-0625 Round Stainless Steel Bar - Type 410 |
/Asset/Bars2.jpg 410-0938 Round Stainless Steel Bar - Type 410 |
/Asset/Bars2.jpg 410-125 Round Stainless Steel Bar - Type 410 |
/Asset/Bars2.jpg 410-1563 Round Stainless Steel Bar - Type 410 |
/Asset/Bars2.jpg 410-1875 Round Stainless Steel Bar - Type 410 |
|||||
| Material | Type 410 Stainless Steel | |||||||||
| Shapeform | Round Bar | |||||||||
| Diameter | 1/16 inches | 3/32 inches | 1/8 inches | 5/32 inches | 3/16 inches | |||||
| Diameter | 0.0625 inches1.5875 mm | 0.0938 inches2.38252 mm | 0.125 inches3.175 mm | 0.1563 inches3.97002 mm | 0.1875 inches4.7625 mm | |||||
| Weight | 0.010 lbs/ft0.01488 kg/m | 0.0240 lbs/ft0.035712 kg/m | 0.042 lbs/ft0.062496 kg/m | 0.065 lbs/ft0.09672 kg/m | 0.094 lbs/ft0.139872 kg/m | |||||
| Finish | No. 2B | |||||||||
| Condition | Fully Heat Treated | |||||||||
| Nominal Composition | 0 or trace Nickel 0.06 to 0.120% Carbon 12% Chrome | |||||||||
| ASTM Specification | UNS SS4100 | |||||||||
| Steel Alloy Group | Martensitic | |||||||||
| Magnetic Properties | Magnetic | |||||||||
| Harden By | Heat Treat | |||||||||
| Corrosion Resistance | Low | |||||||||
| Hardness | High | |||||||||
| Strength | High | |||||||||
| Ductility | Low | |||||||||
| Toughness | Med. | |||||||||
| Elec. Conductance | Med. | |||||||||
| Thermal Conductance | Med. | |||||||||
| Thermal Expansion | Med. | |||||||||
| Heat Resistance (Scaling Strength) | Low/Med. | |||||||||
| Yield Strength | 80000 psi | |||||||||
| Tensile Strength | 100000 psi | |||||||||
| Elongation percent in 2 inches | 20 % | |||||||||
| Hardness (Rockwell B) | 16 to 22 | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1000°F | 9000 lbs/in² | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1100°F | 4200 lbs/in² | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1200°F | 4000 lbs/in² | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1300°F | 1000 lbs/in² | |||||||||
| Density | 0.28 lbs/in³ | |||||||||
| Modulus of Elasticity in Tension | 29.0 x 10-6 lbs/in² | |||||||||
| Specific Heat (32 to 212°F) | 0.11 BTU/ºF/lbs | |||||||||
| Thermal Conductivity at 212°F | 14.4 BTU/hr.ft²/ft/ºF | |||||||||
| Thermal Conductivity at 932°F | 16.6 BTU/hr.ft²/ft/ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 212°F) | 9.3 x 10-6 ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 600°F) | 9.5 x 10-6 ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 1000°F) | 10.3 x 10-6 ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 1200°F) | 10.7 x 10-6 ºF | |||||||||
| Melting Point Range | 2700 to 2790 ºF | |||||||||
| Electrical Resistivity | 57 µΩ.cm | |||||||||
| Max. Operating Temp. (Continuous Service) | 1250 ºF | |||||||||
| Max. Operating Temp. (Intermittent Service) | 1400 ºF | |||||||||
| Welding Properties | Fair-Preheat 400-500°F, Anneal 1250°F after welding | |||||||||
| Drawing and Stamping | Fair-Good | |||||||||
| Hot Working - Initial Forging | 2000 to 2200 ºF | |||||||||
| Annealing Temp. | 1500 to 1650 ºF | |||||||||
| Applications |
|
|||||||||
|
|
||||||||||