Inconel 617 is a nickel-chromium-cobalt-molybdenum alloy with an exceptional combination of metallurgical stability, strength and oxidation resistance at high temperatures. Resistance to oxidation is enhanced by an aluminum addition. Inconel 617 also resists a wide range of corrosive aqueous environments. Inconel 617 is used in gas turbines for combustion cans, ducting and transition liners; for petrochemical processing; for heat-treating equipment; and in nitric acid production. Standard product forms are round, forging stock, extruded section, plate, sheet, strip, pipe, tube and wire.
Request Information
Unit of Measure
Items
Nickel and High Temperature Alloy Plate

Inconel® 617 Plate
Nickel and High Temperature Alloy Plate

Inconel® 617 Plate
Nickel and High Temperature Alloy Plate

Inconel® 617 Plate
Nickel and High Temperature Alloy Plate

Inconel® 617 Plate
Nickel and High Temperature Alloy Plate

Inconel® 617 Plate
Material N/A Inconel®
Shapeform N/A Plates
Thickness N/A 3/16 inches N/A 1/4 inches N/A 3/8 inches N/A 1/2 inches N/A 5/8 inches
Thickness N/A 0.1875 inches4.75 mm N/A 0.25 inches6.3500 mm N/A 0.375 inches9.52 mm N/A 0.500 inches12.7 mm N/A 0.625 inches15.87 mm
Plate Weight per Unit Area N/A 0.06315 lbs/in²44.39884524 kg/m² N/A 0.08317 lbs/in²58.474298632 kg/m² N/A 0.12245 lbs/in²86.09087252 kg/m² N/A 0.16018 lbs/in²112.617688528 kg/m² N/A 0.20023 lbs/in²140.775626008 kg/m²
Alloy N/A Inconel® 617
Basic Composition N/A 1.2% Aluminum 1.5% Iron 125% Cobalt 22.0% Chrominum 52.0% Nickel 9.0% Molybdenum
Density N/A 0.302 lbs/in³8.36 g/cm³
ASTM Specification N/A ASME SB-166(w) ASTM B166(w) SAE 5887 UNS N06617
Melting Temperature Range N/A 2430 to 2510 ºF1330 to 1380 ºC
Rupture Strength (1000 h at 1200°F/650°C) N/A 47000 psi320 MPa
Rupture Strength (1000 h at 1400°F/760°C) N/A 22000 psi150 MPa
Rupture Strength (1000 h at 1600°F/870°C) N/A 8400 psi58 MPa
Rupture Strength (1000 h at 1800°F/980°C) N/A 3600 psi25 MPa
Rupture Strength (1000 h at 2000°F/1095°C) N/A 1500 psi10 MPa