| Items |
 M400-018 Monel® 400 Sheet |
M400-021 Monel® 400 Sheet |
M400-025 Monel® 400 Sheet |
M400-031 Monel® 400 Sheet |
M400-035 Monel® 400 Sheet |
|||||
| Material | Monel® | |||||||||
| Shapeform | Sheets | |||||||||
| Thickness | 0.018 inches0.4572 mm | 0.021 inches0.5334 mm | 0.025 inches0.6350 mm | 0.031 inches0.7874 mm | 0.035 inches0.8890 mm | |||||
| Alloy | Monel 400 | |||||||||
| Basic Composition | 1.1% Manganese 1.6% Iron 32.0% Copper 65.1% Nickel | |||||||||
| Density | 0.319 lbs/in³8.84 g/cm³ | |||||||||
| ASTM Specification | ASME SB-127 ASTM B127 Federal/Military QQ-N 281 CLA SAE 4544 UNS N04400 | |||||||||
| Tensile Strength | 80000 psi550 MPa | |||||||||
| Yield Strength (0.2% Offset) | 35000 psi240 MPa | |||||||||
| Elongation | 40 % | |||||||||
| Melting Temperature Range | 2370 to 2460 ºF1300 to 1350 ºC | |||||||||
|
|
||||||||||