| Items |
 I800HT-025 Incoloy® 800HT Sheet |
I800HT-060 Incoloy® 800HT Sheet |
I800HT-062 Incoloy® 800HT Sheet |
I800HT-093 Incoloy® 800HT Sheet |
I800HT-104 Incoloy® 800HT Sheet |
|||||
| Material | Incoloy® | |||||||||
| Shapeform | Sheets | |||||||||
| Thickness | 0.025 inches0.6350 mm | 0.060 inches1.524 mm | 0.062 inches1.5748 mm | 0.093 inches2.3622 mm | 0.104 inches2.6416 mm | |||||
| Alloy | Incoloy 800HT | |||||||||
| Basic Composition | 0.015% Max. Sulphur 0.10% Carbon 0.60% Aluminum 0.60% Titanium 0.75% Max. Copper 1.0% Max. Silicon 1.20% Aluminum +Titanium 1.50% Max. Manganese 23.0% Chrominum 35.0% Nickel 39.5% Min. Iron | |||||||||
| Density | 0.287 lbs/in³7.94 g/cm³ | |||||||||
| ASTM Specification | ASME SB-409 ASTM B409 UNS N08811 | |||||||||
| Melting Temperature Range | 2475 to 2525 ºF1357 to 1385 ºC | |||||||||
| Rupture Strength (1000 h at 1200°F/650°C) | 24000 psi165 MPa | |||||||||
| Rupture Strength (1000 h at 1300°F/705°C) | 15000 psi105 MPa | |||||||||
| Rupture Strength (1000 h at 1400°F/760°C) | 10000 psi70 MPa | |||||||||
| Rupture Strength (1000 h at 1600°F/870°C) | 4700 psi32 MPa | |||||||||
| Rupture Strength (1000 h at 1800°F/980°C) | 2000 psi14 MPa | |||||||||
|
|
||||||||||