Anodized Aluminum Sheet and Coil

5005 alloy is generally considered to be an improved version of 3003. It has the same general mechanical properties as 3003 but appears to stand up better in actual service. It is readily workable. It can be deep drawn or spun, welded or brazed. It has excellent corrosion resistance. It is non heat-treatable. It is well suited for anodizing and has less tendency to streak or discolor. Applications: cooking utensils, decorative trim, awnings, siding, storage tanks, chemical equipment.

5005-H34
Satin Clear Finish
Paper Interleaved Sheet
Coating Thickness 201R1
201R1 is Exterior Standard No. 1/201 = 0.0002 minimum coating thickness/R1 = Medium Matte

Request Information

Unit of Measure

Items	5005-H34A-032-48-C Anodized Aluminum Sheet and Coil	5005-H34A-032-48-120 Anodized Aluminum Sheet and Coil	5005-H34A-040-48-C Anodized Aluminum Sheet and Coil	5005-H34A-040-48-120 Anodized Aluminum Sheet and Coil	5005-H34A-050-48-C Anodized Aluminum Sheet and Coil
Material	N/A Aluminum
Shapeform	N/A Coil	N/A Sheets	N/A Coil	N/A Sheets	N/A Coil
Series	N/A 5005-H34
Grade	N/A 5005
Preparation	N/A Paper Interleaved
Temper	N/A H34
Finish	N/A Satin Clear
Thickness	N/A 0.032 inches0.8128 mm	N/A 0.032 inches0.8128 mm	N/A 0.040 inches1.016 mm	N/A 0.040 inches1.016 mm	N/A 0.050 inches1.27 mm
Size	N/A 48 x Coil	N/A 48 x 120	N/A 48 x Coil	N/A 48 x 120	N/A 48 x Coil
Width	N/A 48
Length	N/A	N/A 120	N/A	N/A 120	N/A
Sheet Weight per Unit Area	N/A 0.452 lbs/ft²2.207 kg/m²	N/A	N/A 0.564 lbs/ft²2.754 kg/m²	N/A	N/A 0.706 lbs/ft²3.447 kg/m²
Weight per Sheet	N/A	N/A 18.06 lbs8.192 kg	N/A	N/A 22.58 lbs10.242 kg	N/A
Coil Weight per Length	N/A 1.806 lbs/ft2.688 kg/m	N/A	N/A 2.258 lbs/ft3.3608 kg/m	N/A	N/A 2.822 lbs/ft4.120 kg/m
Ultimate Strength	N/A 23 ksi
Yield Strength	N/A 20 ksi
Elongation percent in 2 inches	N/A 8
Hardness Brinnel Number	N/A 41
Ultimate Shearing Strength	N/A 14 ksi
Modulus of Elasticity¹	N/A 10.0 x 10⁶ ksi
Resistance to Corrosion - General²	N/A A
Stress Corrosion Cracking³	N/A A
Workability (Cold)⁴	N/A B
Mechinability	N/A D
Brazeability⁵	N/A B
Gas Weldability⁶	N/A A
Arc Weldability⁷	N/A A
Resistance Spot and Seam Weldability⁸	N/A A
Applications	N/A Appliances, utensils, architectural, electrical conductor
Density	N/A 0.098 lbs/in³
Specific Gravity	N/A 2.70
¹ Average of tension and compression moduli. Compression modulus is about 2 percent greater than tension modulus. ² Ratings A through E are relative ratings in decreasing order of merit, based on exposures to sodium chloride solution by intermittent spraying or immersion. Alloys with A and B ratings can be used in industrial and seacoast atmospheres without protection. Alloys with C, D and E ratings generally should be protected at least on faying surfaces. ³ Stress-corrosion cracking ratings are based on service experience and on laboratory tests of specimens exposed to the 3.5% sodium chloride alternate immersion test. ⁴ Ratings A through D for Workability (cold), and A through E for Machinability, are relative ratings in decreasing order of merit. ⁵ Ratings A through D for Weldability and Brazeability are relative ratings. ⁶ A = Generally weldable by all commercial procedures and methods. B = Weldable with special techniques or for specific applications that justify preliminary trials or testing to develop welding procedure and weld performance. C = Limited weldability because of crack sensitivity or loss in resistance to corrosion and mechanical properties. ⁷ A = Generally weldable by all commercial procedures and methods. B = Weldable with special techniques or for specific applications that justify preliminary trials or testing to develop welding procedure and weld performance. C = Limited weldability because of crack sensitivity or loss in resistance to corrosion and mechanical properties. ⁸ A = Generally weldable by all commercial procedures and methods. B = Weldable with special techniques or for specific applications that justify preliminary trials or testing to develop welding procedure and weld performance. C = Limited weldability because of crack sensitivity or loss in resistance to corrosion and mechanical properties.