Hot Rolled, Annealed and Pickled
A.S.T.M. A240/A480 ASME SA-240
Unit of Measure
Specifications
|
Typical Mechanical Properties
|
Comparative Characteristics and Applications
|
Applications
Specifications
Material |
N/A Type 317L Stainless Steel |
Shapeform |
N/A Plates |
Thickness |
N/A 1 1/2 inches |
Thickness |
N/A 1.500 inches38.1 mm |
Size |
N/A 96 x 240 inches |
Width |
N/A 96 inches |
Length |
N/A 240 inches |
Weight per Plate |
N/A 10134 lbs4596.7053816 kg |
Finish |
N/A No. 2B |
Condition |
N/A Hot Rolled Annealed Pickled |
Nominal Composition |
N/A 0.08% Max. Carbon 1.00% Max. Silicon 11.00 to 15.00% Nickel 18.00 to 20.00% Chrominum 2.0 to 3.0% Molybdenum 2.00% Max. Manganese |
ASTM Specification |
N/A ASME SA-240 ASTM A240 ASTM A480 UNS S31703 |
Typical Mechanical Properties
Steel Alloy Group |
N/A Austenitic |
Magnetic Properties |
N/A Non-Magnetic |
Harden By |
N/A Cold Work |
Corrosion Resistance |
N/A High |
Hardness |
N/A Low to Med. |
Strength |
N/A Low to Med. |
Ductility |
N/A High |
Toughness |
N/A High |
Elec. Conductance |
N/A Low |
Thermal Conductance |
N/A Low |
Thermal Expansion |
N/A High |
Heat Resistance (Scaling Strength) |
N/A High/High |
Comparative Characteristics and Applications
Density |
N/A 0.29 lbs/in³ |
Modulus of Elasticity in Tension |
N/A 28.0 x 106 lbs/in² |
Specific Heat (32 to 212°F) |
N/A 0.12 BTU/ºF/lbs |
Thermal Conductivity at 212°F |
N/A 9.4 BTU/hr.ft²/ft/ºF |
Thermal Conductivity at 932°F |
N/A 12.4 BTU/hr.ft²/ft/ºF |
Mean Coefficient of Thermal Expansion per °F (32 to 212°F) |
N/A 8.9 x 10-6 ºF |
Mean Coefficient of Thermal Expansion per °F (32 to 600°F) |
N/A 9.0 x 10-6 ºF |
Mean Coefficient of Thermal Expansion per °F (32 to 1000°F) |
N/A 9.7 x 10-6 ºF |
Mean Coefficient of Thermal Expansion per °F (32 to 1200°F) |
N/A 10.3 x 10-6 ºF |
Melting Point Range |
N/A 2500 to 2550 ºF |
Electrical Resistivity |
N/A 74 µΩ.cm |
Max. Operating Temp. (Continuous Service) |
N/A 1700 ºF |
Max. Operating Temp. (Intermittent Service) |
N/A 1600 ºF |
Welding Properties |
N/A Very Good-Tough Welds |
Drawing and Stamping |
N/A Good |
Hot Working - Initial Forging |
N/A 2100 to 2300 ºF |
Annealing Temp. |
N/A 1850 to 2050 ºF |
Stress Relieving Temp. |
N/A 400 to 750 ºF |
Applications
|
N/A
|