Inconel 617 is a nickel-chromium-cobalt-molybdenum alloy with an exceptional combination of metallurgical stability, strength and oxidation resistance at high temperatures. Resistance to oxidation is enhanced by an aluminum addition. Inconel 617 also resists a wide range of corrosive aqueous environments. Inconel 617 is used in gas turbines for combustion cans, ducting and transition liners; for petrochemical processing; for heat-treating equipment; and in nitric acid production. Standardmore
Unit of Measure

Specifications

Material

Inconel®

Shapeform

Plates

Thickness

2 1/2 inches

Thickness

2.500 inches63.5 mm

Plate Weight per Unit Area

0.79323 lbs/in²557.695898808 kg/m²

Nickel Alloy Compositions

Alloy

Inconel® 617

Basic Composition

1.2% Aluminum 1.5% Iron 125% Cobalt 22.0% Chrominum 52.0% Nickel 9.0% Molybdenum

Density

0.302 lbs/in³8.36 g/cm³

ASTM Specification

ASME SB-166(w) ASTM B166(w) SAE 5887 UNS N06617

Typical Mechanical Properties

Melting Temperature Range

2430 to 2510 ºF1330 to 1380 ºC

Rupture Strength (1000 h at 1200°F/650°C)

47000 psi320 MPa

Rupture Strength (1000 h at 1400°F/760°C)

22000 psi150 MPa

Rupture Strength (1000 h at 1600°F/870°C)

8400 psi58 MPa

Rupture Strength (1000 h at 1800°F/980°C)

3600 psi25 MPa

Rupture Strength (1000 h at 2000°F/1095°C)

1500 psi10 MPa