1100 grade is commercially pure aluminum. It is soft and ductile and has excellent workability. It is ideal for applications involving intricate forming because it work hardens more slowly than other alloys. It is the most weldable of aluminum alloys, by any method. It is non heat-treatable. It has excellent resistance to corrosion and is widely used in the chemical and food processing industries. It responds well to decorative finishes which make it suitable for giftware.

1100-H14
Mill Finish
AMS-QQ-A-250/1 AMS4003 ASTM B209
Unit of Measure

Specifications

Material

N/A Aluminum

Shapeform

N/A Coil

Series

N/A 1100-H14

Grade

N/A 1100

Temper

N/A H14

Finish

N/A Mill

Thickness

N/A 0.016 inches0.4064 mm

Size

N/A 36 x Coil

Width

N/A 36

Sheet Weight per Unit Area

N/A 0.226 lbs/ft²1.103 kg/m²

Coil Weight per Length

N/A 0.677 lbs/ft1.007 kg/m

ASTM Specification

N/A AMS 4003 AMS-QQ-A-250/1 ASME SB-209 ASTM B209

Density

N/A 0.098 lbs/in³

Specific Gravity

N/A 2.71

Typical Mechanical Properties

Ultimate Strength

N/A 18 ksi

Yield Strength

N/A 17 ksi

Elongation percent in 2 inches

N/A 9

Hardness Brinnel Number

N/A 32

Ultimate Shearing Strength

N/A 11 ksi
Fatigue Endurance Limit1 N/A 7 ksi
Modulus of Elasticity2 N/A 10.0 x 106 ksi

Comparative Characteristics and Applications

Resistance to Corrosion - General3 N/A A
Stress Corrosion Cracking4 N/A A
Workability (Cold)5 N/A A

Mechinability

N/A D
Brazeability6 N/A A
Gas Weldability7 N/A A
Arc Weldability8 N/A A
Resistance Spot and Seam Weldability9 N/A A

Applications

N/A Sheet metal work, spun hollowware, fin stock

Aluminum Alloy Designations

N/A

    The aluminum industry uses a four-digit index system for the designation of its wrought aluminum alloys.
    As outlined below, the first digit indicates the alloy group according to the major alloying elements.

    1xxx Series
    In this group minimum aluminum content is 99% and there is no major alloying element. The second digit indicates modifications in impurity limits. If the second digit is zero, there is no special control on individual impurities. Digits 1 through 9, which are assigned consecutively as needed, indicate special control of one or more individual impurities. The last two digits indicate specific minimum aluminum content. Although the absolute minimum aluminum content in this group is 99%, the minimum for certain grades is higher than 99%, and the last two digits represent the hundredths of a per cent over 99. Thus, 1030 would indicate 99.30% minimum aluminum. without special control on individual impurities. The designations 1130, 1230, 1330, etc.. indicate the same purity with special control on one or more impurities. Likewise 1100 indicates minimum aluminum content of 99.00% with individual impurity control.

    2xxx through 9xxx Series
    The major alloying elements are indicated by the first digit, as follows:
      2xxx Copper
      3xxx Manganese
      4xxx Silicon
      5xxx Magnesium
      6xxx Magnesium and silicon
      7xxx Zinc
      8xxx Other element
      9xxx Unused series

    The second digit indicates alloy modification. If the second digit is zero. it indicates the original alloy: digits 1 through 9, which are assigned consecutively, indicate alloy modifications. The last two digits have no special significance, serving only to identify the different alloys in the group.

    Experimental Alloys
    Experimental alloys are designated according to the four digit system, but they are prefixed by the letter X. The prefix is dropped when the alloy becomes standard. During development, and before they are designated as experimental, new alloys are identified by serial numbers assigned by their originators. Use of the serial number is discontinued when the X number is assigned.

  • 1 Based on 500000.000 cycles of completely reversed stress using the R. R. Moore-type of machine and specimen.
  • 2 Average of tension and compression moduli. Compression modulus is about 2 percent greater than tension modulus.
  • 3 Ratings A through E are relative ratings in decreasing order of merit, based on exposures to sodium chloride solution by intermittent spraying or immersion. Alloys with A and B ratings can be used in industrial and seacoast atmospheres without protection. Alloys with C, D and E ratings generally should be protected at least on faying surfaces.
  • 4 Stress-corrosion cracking ratings are based on service experience and on laboratory tests of specimens exposed to the 3.5% sodium chloride alternate immersion test.
  • 5 Ratings A through D for Workability (cold), and A through E for Machinability, are relative ratings in decreasing order of merit.
  • 6 Ratings A through D for Weldability and Brazeability are relative ratings.
  • 7 A = Generally weldable by all commercial procedures and methods.
    B = Weldable with special techniques or for specific applications that justify preliminary trials or testing to develop welding procedure and weld performance.
    C = Limited weldability because of crack sensitivity or loss in resistance to corrosion and mechanical properties.
  • 8 A = Generally weldable by all commercial procedures and methods.
    B = Weldable with special techniques or for specific applications that justify preliminary trials or testing to develop welding procedure and weld performance.
    C = Limited weldability because of crack sensitivity or loss in resistance to corrosion and mechanical properties.
  • 9 A = Generally weldable by all commercial procedures and methods.
    B = Weldable with special techniques or for specific applications that justify preliminary trials or testing to develop welding procedure and weld performance.
    C = Limited weldability because of crack sensitivity or loss in resistance to corrosion and mechanical properties.