2024-T4 2024-T351
Screw Machine Stock Sizes Under 5/8" Supplied in T4
AMS-QQ-A-225/6 (6 1/2" max) AMS 4120
ASTM B211 UNS A92024
Specifications
Material |
N/A Aluminum |
Shapeform |
N/A Round |
Series |
N/A 2024-T4 |
Grade |
N/A 2024 |
Temper |
N/A T4 |
Diameter |
N/A 7/16 inches |
Diameter |
N/A 0.4375 inches11.1125 mm |
Estimated Weight |
N/A 0.1800 lbs/ft0.267876 kg/m |
Estimated Weight per 12' Bar |
N/A 2.165 lbs0.982027546 kg |
ASTM Specification |
N/A AMS 4120 AMS-QQ-A-225/6 ASTM B211 UNS A92024 |
Ultimate Strength |
N/A 68 ksi |
Yield Strength |
N/A 47 ksi |
Density |
N/A 0.100 lbs/in³ |
Specific Gravity |
N/A 2.78 |
Typical Mechanical Properties
Elongation percent in 2 inches |
N/A 19 |
Hardness Brinnel Number |
N/A 120 |
Ultimate Shearing Strength |
N/A 41 ksi |
Fatigue Endurance Limit1 | N/A 20 ksi |
Modulus of Elasticity2 | N/A 10.6 x 104 ksi |
Comparative Characteristics and Applications
Resistance to Corrosion - General3 | N/A D |
Stress Corrosion Cracking4 | N/A C |
Workability (Cold)5 | N/A C |
Mechinability |
N/A B |
Brazeability6 | N/A D |
Gas Weldability7 | N/A C |
Arc Weldability8 | N/A B |
Resistance Spot and Seam Weldability9 | N/A B |
Applications |
N/A Truck wheels, screw machine products, aircraft structures |
Aluminum Alloy Designations
N/A
|
- 1 Based on 500,000.000 cycles of completely reversed stress using the R. R. Moore-type of machine and specimen.
- 2 Average of tension and compression moduli. Compression modulus is about 2 percent greater than tension modulus.
-
3 Ratings A through E are relative ratings in decreasing order of merit, based on exposures to sodium chloride solution by intermittent spraying or immersion. Alloys with A and B ratings can be used in industrial and seacoast atmospheres without protection. Alloys with C, D and E ratings generally should be protected at least on faying surfaces.
Inrelatively thick sections, rating would be E. - 4 Stress-corrosion cracking ratings are based on service experience and on laboratory tests of specimens exposed to the 3.5% sodium chloride alternate immersion test.
- 5 Ratings A through D for Workability (cold), and A through E for Machinability, are relative ratings in decreasing order of merit.
- 6 Ratings A through D for Weldability and Brazeability are relative ratings.
-
7 A = Generally weldable by all commercial procedures and methods.
B = Weldable with special techniques or for specific applications that justify preliminary trials or testing to develop welding procedure and weld performance.
C = Limited weldability because of crack sensitivity or loss in resistance to corrosion and mechanical properties. -
8 A = Generally weldable by all commercial procedures and methods.
B = Weldable with special techniques or for specific applications that justify preliminary trials or testing to develop welding procedure and weld performance.
C = Limited weldability because of crack sensitivity or loss in resistance to corrosion and mechanical properties. -
9 A = Generally weldable by all commercial procedures and methods.
B = Weldable with special techniques or for specific applications that justify preliminary trials or testing to develop welding procedure and weld performance.
C = Limited weldability because of crack sensitivity or loss in resistance to corrosion and mechanical properties.