| Items |
 316SB-125 Square Stainless Steel Bar - Type 316 |
316SB-1875 Square Stainless Steel Bar - Type 316 |
316SB-250 Square Stainless Steel Bar - Type 316 |
316SB-3125 Square Stainless Steel Bar - Type 316 |
316SB-375 Square Stainless Steel Bar - Type 316 |
|||||
| Material | Type 316 Stainless Steel | |||||||||
| Shapeform | Square Bar | |||||||||
| Size | 1/8 inches | 3/16 inches | 1/4 inches | 5/16 inches | 3/8 inches | |||||
| Size | 0.125 inches3.175 mm | 0.1875 inches4.7625 mm | 0.25 inches6.35 mm | 0.3125 inches7.9375 mm | 0.375 inches9.525 mm | |||||
| Weight | 0.0531 lbs/ft0.0790128 kg/m | 0.1196 lbs/ft0.1779648 kg/m | 0.2126 lbs/ft0.3163488 kg/m | 0.3321 lbs/ft0.4941648 kg/m | 0.4782 lbs/ft0.7115616 kg/m | |||||
| Weight per 12' Length | 0.638 lbs0.289014 kg | 1.435 lbs0.650055 kg | 2.551 lbs1.155603 kg | 3.985 lbs1.805205 kg | 5.739 lbs2.599767 kg | |||||
| Finish | No. 2B | |||||||||
| Condition | Cold Drawn Annealed | |||||||||
| Nominal Composition | 0 to 0.25% Carbon 1.00% Max. Silicon 2.00% Max. Manganese 6 to 36% Nickel 7 to 30% Chrome | |||||||||
| ASTM Specification | ASTM A276 UNS S31600 | |||||||||
| Random Length | 10 to 14 ft | |||||||||
| Steel Alloy Group | Austenitic | |||||||||
| Magnetic Properties | Non-Magnetic | |||||||||
| Harden By | Cold Work | |||||||||
| Corrosion Resistance | High | |||||||||
| Hardness | Low to Med. | |||||||||
| Strength | Low to Med. | |||||||||
| Ductility | High | |||||||||
| Toughness | High | |||||||||
| Elec. Conductance | Low | |||||||||
| Thermal Conductance | Low | |||||||||
| Thermal Expansion | High | |||||||||
| Heat Resistance (Scaling Strength) | High/High | |||||||||
| Yield Strength | 45000 lbs/in² | |||||||||
| Tensile Strength | 18200 lbs/in² | |||||||||
| Elongation percent in 2 inches | 50 % | |||||||||
| Hardness (Rockwell B) | 83 | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1000°F | 25000 lbs/in² | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1100°F | 18200 lbs/in² | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1200°F | 12700 lbs/in² | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1300°F | 7900 lbs/in² | |||||||||
| Density | 0.29 lbs/in³ | |||||||||
| Modulus of Elasticity in Tension | 29.0 x 106 lbs/in² | |||||||||
| Specific Heat (32 to 212°F) | 0.12 BTU/ºF/lbs | |||||||||
| Thermal Conductivity at 212°F | 9.4 BTU/hr.ft²/ft/ºF | |||||||||
| Thermal Conductivity at 932°F | 12.4 BTU/hr.ft²/ft/ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 212°F) | 8.8 x 10-6 ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 600°F) | 9.0 x 10-6 ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 1000°F) | 9.7 x 10-6 ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 1200°F) | 10.3 x 10-6 ºF | |||||||||
| Melting Point Range | 2500 to 2550 ºF | |||||||||
| Electrical Resistivity | 74 µΩ.cm | |||||||||
| Max. Operating Temp. (Continuous Service) | 1650 ºF | |||||||||
| Max. Operating Temp. (Intermittent Service) | 1500 ºF | |||||||||
| Welding Properties | Very Good-Tough Welds | |||||||||
| Drawing and Stamping | Good | |||||||||
| Hot Working - Initial Forging | 2100 to 2300 ºF | |||||||||
| Annealing Temp. | 1850 to 2050 ºF | |||||||||
| Stress Relieving Temp. | 400 to 750 ºF | |||||||||
| Applications |
|
|||||||||
|
|
||||||||||