| Items |
 I601-1875 Inconel® 601 Plate |
I601-250 Inconel® 601 Plate |
I601-3125 Inconel® 601 Plate |
I601-3750 Inconel® 601 Plate |
I601-500 Inconel® 601 Plate |
|||||
| Material | Inconel® | |||||||||
| Shapeform | Plates | |||||||||
| Thickness | 3/16 inches | 1/4 inches | 5/16 inches | 3/8 inches | 1/2 inches | |||||
| Thickness | 0.1875 inches4.7625 mm | 0.25 inches6.3500 mm | 0.3125 inches7.9375 mm | 0.375 inches9.5250 mm | 0.500 inches12.7 mm | |||||
| Plate Weight per Unit Area | 0.0595 lbs/in²41.8326412 kg/m² | 0.0795 lbs/in²55.8940332 kg/m² | 0.0995 lbs/in²69.9554252 kg/m² | 0.118 lbs/in²82.9622128 kg/m² | 0.156 lbs/in²109.6788576 kg/m² | |||||
| Alloy | Inconel® 601 | |||||||||
| Basic Composition | 1.4% Aluminum 14.4% Iron 23.0% Chrominum 60.5% Nickel | |||||||||
| Density | 0.291 lbs/in³8.06 g/cm³ | |||||||||
| ASTM Specification | ASME SB-168 ASTM B168 SAE 5870 UNS N06601 | |||||||||
| Melting Temperature Range | 2480 to 2571 ºF1360 to 1411 ºC | |||||||||
| Rupture Strength (1000 h at 1200°F/650°C) | 28000 psi195 MPa | |||||||||
| Rupture Strength (1000 h at 1400°F/760°C) | 9100 psi63 MPa | |||||||||
| Rupture Strength (1000 h at 1600°F/870°C) | 4300 psi30 MPa | |||||||||
| Rupture Strength (1000 h at 1800°F/980°C) | 2100 psi14 MPa | |||||||||
| Rupture Strength (1000 h at 2000°F/1095°C) | 1000 psi7 MPa | |||||||||
|
|
||||||||||