| Items |
 I601-040 Inconel® 601 Sheet |
I601-043 Inconel® 601 Sheet |
I601-050 Inconel® 601 Sheet |
I601-060 Inconel® 601 Sheet |
I601-062 Inconel® 601 Sheet |
|||||
| Material | Inconel® | |||||||||
| Shapeform | Sheets | |||||||||
| Thickness | 0.040 inches1.016 mm | 0.043 inches1.0922 mm | 0.050 inches1.27 mm | 0.060 inches1.524 mm | 0.062 inches1.5748 mm | |||||
| Alloy | Inconel® 601 | |||||||||
| Basic Composition | 1.4% Aluminum 14.4% Iron 23.0% Chrominum 60.5% Nickel | |||||||||
| Density | 0.291 lbs/in³8.06 g/cm³ | |||||||||
| ASTM Specification | ASME SB-168 ASTM B168 SAE 5870 UNS N06601 | |||||||||
| Melting Temperature Range | 2480 to 2571 ºF1360 to 1411 ºC | |||||||||
| Rupture Strength (1000 h at 1200°F/650°C) | 28000 psi195 MPa | |||||||||
| Rupture Strength (1000 h at 1400°F/760°C) | 9100 psi63 MPa | |||||||||
| Rupture Strength (1000 h at 1600°F/870°C) | 4300 psi30 MPa | |||||||||
| Rupture Strength (1000 h at 1800°F/980°C) | 2100 psi14 MPa | |||||||||
| Rupture Strength (1000 h at 2000°F/1095°C) | 1000 psi7 MPa | |||||||||
|
|
||||||||||