Painted Aluminum Sheet - Series 3105-H14

Unit of Measure

Items	3105-H14-019-48-C Painted Aluminum Sheet - Series 3105-H14	3105-H14-019-48-96 Painted Aluminum Sheet - Series 3105-H14	3105-H14-024-36-C Painted Aluminum Sheet - Series 3105-H14	3105-H14-024-36-120 Painted Aluminum Sheet - Series 3105-H14	3105-H14-025-36-C Painted Aluminum Sheet - Series 3105-H14
Material	N/A Aluminum
Shapeform	N/A Coil	N/A Sheets	N/A Coil	N/A Sheets	N/A Coil
Series	N/A 3105-H14
Grade	N/A 3105
Temper	N/A H14
Thickness	N/A 0.019 inches0.4826 mm	N/A 0.019 inches0.4826 mm	N/A 0.024 inches0.6096 mm	N/A 0.024 inches0.6096 mm	N/A 0.025 inches0.6350 mm
Size	N/A 48 x Coil	N/A 48 x 96	N/A 36 x Coil	N/A 36 x 120	N/A 36 x Coil
Width	N/A 48	N/A 48	N/A 36	N/A 36	N/A 36
Length	N/A	N/A 96	N/A	N/A 120	N/A
Sheet Weight per Unit Area	N/A 0.276 lbs/ft²1.347432 kg/m²	N/A 0.276 lbs/ft²1.347432 kg/m²	N/A 0.347 lbs/ft²1.694054 kg/m²	N/A 0.347 lbs/ft²1.694054 kg/m²	N/A 0.369 lbs/ft²1.801458 kg/m²
Weight per Sheet	N/A	N/A 8.83 lbs3.99999 kg	N/A	N/A 10.41 lbs4.71573 kg	N/A
Ultimate Strength	N/A 25 ksi
Yield Strength	N/A 22 ksi
Elongation percent in 2 inches	N/A 5
Ultimate Shearing Strength	N/A 15 ksi
Modulus of Elasticity¹	N/A 10.0 x 10² ksi
Resistance to Corrosion - General²	N/A A
Stress Corrosion Cracking³	N/A A
Workability (Cold)⁴	N/A B
Mechinability	N/A D
Brazeability⁵	N/A A
Gas Weldability⁶	N/A A
Arc Weldability⁷	N/A A
Resistance Spot and Seam Weldability⁸	N/A A
Applications	N/A Residential siding, mobile homes, rain carrying goods, sheet metal work
Density	N/A 0.098 lbs/in³
Specific Gravity	N/A 2.72
¹ Average of tension and compression moduli. Compression modulus is about 2 percent greater than tension modulus. ² Ratings A through E are relative ratings in decreasing order of merit, based on exposures to sodium chloride solution by intermittent spraying or immersion. Alloys with A and B ratings can be used in industrial and seacoast atmospheres without protection. Alloys with C, D and E ratings generally should be protected at least on faying surfaces. ³ Stress-corrosion cracking ratings are based on service experience and on laboratory tests of specimens exposed to the 3.5% sodium chloride alternate immersion test. ⁴ Ratings A through D for Workability (cold), and A through E for Machinability, are relative ratings in decreasing order of merit. ⁵ Ratings A through D for Weldability and Brazeability are relative ratings. ⁶ A = Generally weldable by all commercial procedures and methods. B = Weldable with special techniques or for specific applications that justify preliminary trials or testing to develop welding procedure and weld performance. C = Limited weldability because of crack sensitivity or loss in resistance to corrosion and mechanical properties. ⁷ A = Generally weldable by all commercial procedures and methods. B = Weldable with special techniques or for specific applications that justify preliminary trials or testing to develop welding procedure and weld performance. C = Limited weldability because of crack sensitivity or loss in resistance to corrosion and mechanical properties. ⁸ A = Generally weldable by all commercial procedures and methods. B = Weldable with special techniques or for specific applications that justify preliminary trials or testing to develop welding procedure and weld performance. C = Limited weldability because of crack sensitivity or loss in resistance to corrosion and mechanical properties.