Aluminum Rectangles - Series 6063-T52

Unit of Measure

Items	6063-T52-125-500 Aluminum Rectangles - Series 6063-T52	6063-T52-125-625 Aluminum Rectangles - Series 6063-T52	6063-T52-125-750 Aluminum Rectangles - Series 6063-T52	6063-T52-125-1000 Aluminum Rectangles - Series 6063-T52	6063-T52-125-1250 Aluminum Rectangles - Series 6063-T52
Material	N/A Aluminum
Shapeform	N/A Rectangles
Series	N/A 6063-T52
Grade	N/A 6063
Temper	N/A T52
Size	N/A 1/8 x 1/2 inches	N/A 1/8 x 5/8 inches	N/A 1/8 x 3/4 inches	N/A 1/8 x 1 inches	N/A 1/8 x 1 1/4 inches
Working Decimal Equivalent	N/A 0.125 x 0.500 inches3.175 x 12.700 mm	N/A 0.125 x 0.625 inches3.175 x 15.875 mm	N/A 0.125 x 0.750 inches3.175 x 19.050 mm	N/A 0.125 x 1.000 inches3.175 x 25.400 mm	N/A 0.125 x 1.250 inches3.175 x 31.750 mm
Width	N/A 1/8 inches
Length	N/A 1/2 inches	N/A 5/8 inches	N/A 3/4 inches	N/A 1 inches	N/A 1 1/4 inches
Estimated Weight	N/A 0.0728 lbs/ft0.1083383392 kg/m	N/A 0.0909 lbs/ft0.1352741076 kg/m	N/A 0.1091 lbs/ft0.1623586924 kg/m	N/A 0.1455 lbs/ft0.216527862 kg/m	N/A 0.1819 lbs/ft0.2706970316 kg/m
Estimated Weight per 12' Bar	N/A 1.164 lbs0.5279815536 kg	N/A 1.455 lbs0.659976942 kg	N/A 1.746 lbs0.7919723304 kg	N/A 2.328 lbs1.0559631072 kg	N/A 2.910 lbs1.319953884 kg
ASTM Specification	N/A ASTM B221
Stock Length	N/A 16 ft
Ultimate Strength	N/A 27 ksi
Yield Strength	N/A 21 ksi
Elongation percent in 2 inches	N/A 12
Hardness Brinnel Number	N/A 60
Ultimate Shearing Strength	N/A 17 ksi
Fatigue Endurance Limit¹	N/A 10 ksi
Modulus of Elasticity²	N/A 10.0 x 10⁴ ksi
Resistance to Corrosion - General³	N/A A
Stress Corrosion Cracking⁴	N/A A
Workability (Cold)⁵	N/A B
Mechinability	N/A C
Brazeability⁶	N/A A
Gas Weldability⁷	N/A A
Arc Weldability⁸	N/A A
Resistance Spot and Seam Weldability⁹	N/A A
Applications	N/A Pipe railing, furniture, architectural extrusions
Density	N/A 0.097 lbs/in³
Specific Gravity	N/A 2.70
¹ Based on 500,000.000 cycles of completely reversed stress using the R. R. Moore-type of machine and specimen. ² Average of tension and compression moduli. Compression modulus is about 2 percent greater than tension modulus. ³ Ratings A through E are relative ratings in decreasing order of merit, based on exposures to sodium chloride solution by intermittent spraying or immersion. Alloys with A and B ratings can be used in industrial and seacoast atmospheres without protection. Alloys with C, D and E ratings generally should be protected at least on faying surfaces. ⁴ Stress-corrosion cracking ratings are based on service experience and on laboratory tests of specimens exposed to the 3.5% sodium chloride alternate immersion test. ⁵ Ratings A through D for Workability (cold), and A through E for Machinability, are relative ratings in decreasing order of merit. ⁶ Ratings A through D for Weldability and Brazeability are relative ratings. ⁷ A = Generally weldable by all commercial procedures and methods. B = Weldable with special techniques or for specific applications that justify preliminary trials or testing to develop welding procedure and weld performance. C = Limited weldability because of crack sensitivity or loss in resistance to corrosion and mechanical properties. ⁸ A = Generally weldable by all commercial procedures and methods. B = Weldable with special techniques or for specific applications that justify preliminary trials or testing to develop welding procedure and weld performance. C = Limited weldability because of crack sensitivity or loss in resistance to corrosion and mechanical properties. ⁹ A = Generally weldable by all commercial procedures and methods. B = Weldable with special techniques or for specific applications that justify preliminary trials or testing to develop welding procedure and weld performance. C = Limited weldability because of crack sensitivity or loss in resistance to corrosion and mechanical properties.