Hot Rolled, Annealed and Pickled
A.S.T.M. A240/A480 ASME SA-240
Specifications
Material |
N/A Type 410S Stainless Steel |
Shapeform |
N/A Plates |
Thickness |
N/A 1/2 inches |
Thickness |
N/A 0.500 inches12.7 mm |
Size |
N/A 96 x 240 inches |
Width |
N/A 96 inches |
Length |
N/A 240 inches |
Plate Weight per Unit Area |
N/A 21.663 lbs/ft²105.758766 kg/m² |
Weight per Plate |
N/A 3466 lbs1572.1512584 kg |
Finish |
N/A No. 2B |
Condition |
N/A Hot Rolled Annealed Pickled |
Nominal Composition |
N/A 0 or trace Nickel 0.06 to 0.35% Carbon 0.75% Max. Titanium x Carbon Min 1.00% Max. Manganese 1.00% Max. Silicon 10.50 to 11.75% Chrominum |
ASTM Specification |
N/A ASME SA-240 ASTM A240 ASTM A480 UNS S41008 |
Typical Mechanical Properties
Steel Alloy Group |
N/A Ferritic |
Magnetic Properties |
N/A Magnetic |
Harden By |
N/A Cold Work |
Corrosion Resistance |
N/A Med. to High |
Hardness |
N/A Low |
Strength |
N/A Low |
Ductility |
N/A Med. |
Toughness |
N/A Low to Med. |
Elec. Conductance |
N/A Med. |
Thermal Conductance |
N/A Med. |
Thermal Expansion |
N/A Med. |
Heat Resistance (Scaling Strength) |
N/A High/Low |
Comparative Characteristics and Applications
Yield Strength |
N/A 49000 lbs/in² |
Tensile Strength |
N/A 70000 lbs/in² |
Elongation percent in 2 inches |
N/A 31 % |
Hardness (Rockwell B) |
N/A 85 |
Creep Strength Load for 10000 Hr. with 1% Elongation at 1000°F |
N/A 9000 lbs/in² |
Creep Strength Load for 10000 Hr. with 1% Elongation at 1100°F |
N/A 4200 lbs/in² |
Creep Strength Load for 10000 Hr. with 1% Elongation at 1200°F |
N/A 4000 lbs/in² |
Creep Strength Load for 10000 Hr. with 1% Elongation at 1300°F |
N/A 1000 lbs/in² |
Density |
N/A 0.28 lbs/in³ |
Modulus of Elasticity in Tension |
N/A 29.0 x 106 lbs/in² |
Specific Heat (32 to 212°F) |
N/A 0.11 BTU/ºF/lbs |
Thermal Conductivity at 212°F |
N/A 14.4 BTU/hr.ft²/ft/ºF |
Thermal Conductivity at 932°F |
N/A 16.6 BTU/hr.ft²/ft/ºF |
Mean Coefficient of Thermal Expansion per °F (32 to 212°F) |
N/A 9.3 x 10-6 ºF |
Mean Coefficient of Thermal Expansion per °F (32 to 600°F) |
N/A 9.5 x 10-6 ºF |
Mean Coefficient of Thermal Expansion per °F (32 to 1000°F) |
N/A 10.3 x 10-6 ºF |
Mean Coefficient of Thermal Expansion per °F (32 to 1200°F) |
N/A 10.7 x 10-6 ºF |
Melting Point Range |
N/A 2700 to 2750 ºF |
Electrical Resistivity |
N/A 57 µΩ.cm |
Max. Operating Temp. (Continuous Service) |
N/A 1250 ºF |
Max. Operating Temp. (Intermittent Service) |
N/A 1400 ºF |
Welding Properties |
N/A Fair-Preheat 400-500°F, Anneal 1250°F after welding |
Drawing and Stamping |
N/A Fair-Good |
Hot Working - Initial Forging |
N/A 2000 to 2200 ºF |
Annealing Temp. |
N/A 1500 to 1650 ºF |
Applications
|