Incoloy 800HT is a nickel-iron-chromium alloy with good strength and excellent resistance to oxidation and carburization in high-temperature atmospheres. It also resists corrosion by many aqueous environments. Incoloy 800HT maintains a stable, austenitic structure during prolonged exposure to high temperatures.
Incoloy 800HT is used for process piping, heat exchangers, carburizing equipment, heating-element sheathing and nuclear steam-generator tubing. Standard product forms are round, flats, forging stock, pipe, tube, plate, sheet, strip and wire.
Unit of Measure
Specifications
Material |
N/A Incoloy® |
Shapeform |
N/A Plates |
Thickness |
N/A 1 inches |
Thickness |
N/A 1.000 inches25.4 mm |
Plate Weight per Unit Area |
N/A 0.29628 lbs/in²208.3054611 kg/m² |
Nickel Alloy Compositions
Alloy |
N/A Incoloy 800HT |
Basic Composition |
N/A 0.015% Max. Sulphur 0.10% Carbon 0.60% Aluminum 0.60% Titanium 0.75% Max. Copper 1.0% Max. Silicon 1.20% Aluminum +Titanium 1.50% Max. Manganese 23.0% Chrominum 35.0% Nickel 39.5% Min. Iron |
Density |
N/A 0.287 lbs/in³7.94 g/cm³ |
ASTM Specification |
N/A ASME SB-409 ASTM B409 UNS N08811 |
Typical Mechanical Properties
Melting Temperature Range |
N/A 2475 to 2525 ºF1357 to 1385 ºC |
Rupture Strength (1000 h at 1200°F/650°C) |
N/A 24000 psi165 MPa |
Rupture Strength (1000 h at 1300°F/705°C) |
N/A 15000 psi105 MPa |
Rupture Strength (1000 h at 1400°F/760°C) |
N/A 10000 psi70 MPa |
Rupture Strength (1000 h at 1600°F/870°C) |
N/A 4700 psi32 MPa |
Rupture Strength (1000 h at 1800°F/980°C) |
N/A 2000 psi14 MPa |