| Material | Type 309S Stainless Steel | |||||||||
| Shapeform | Plates | |||||||||
| Thickness | 3/16 inches | |||||||||
| Thickness | 0.1875 inches4.7625 mm | |||||||||
| Size | 48 x 96 inches | 48 x 120 inches | 48 x 144 inches | 48 x 240 inches | 96 x 240 inches | |||||
| Width | 48 inches | 48 inches | 48 inches | 48 inches | 96 inches | |||||
| Length | 96 inches | 120 inches | 144 inches | 240 inches | 240 inches | |||||
| Plate Weight per Unit Area | 8.579 lbs/ft²41.882678 kg/m² | |||||||||
| Weight per Plate | 275 lbs124.73791 kg | 343 lbs155.5821932 kg | 412 lbs186.8800688 kg | 686 lbs311.1643864 kg | 1373 lbs622.7823652 kg | |||||
| Finish | No. 2B | |||||||||
| Condition | Hot Rolled Annealed Pickled | |||||||||
| Nominal Composition | 0.08% Max. Carbon 1.00% Max. Silicon 12.00 to 15.00% Nickel 2.00% Max. Manganese 22.00 to 24.00% Chrominum | |||||||||
| ASTM Specification | ASME SA-240 ASTM A240 ASTM A480 UNS S30908 | |||||||||
| Steel Alloy Group | Austenitic | |||||||||
| Magnetic Properties | Non-Magnetic | |||||||||
| Harden By | Cold Work | |||||||||
| Corrosion Resistance | High | |||||||||
| Hardness | Low to Med. | |||||||||
| Strength | Low to Med. | |||||||||
| Ductility | High | |||||||||
| Toughness | High | |||||||||
| Elec. Conductance | Low | |||||||||
| Thermal Conductance | Low | |||||||||
| Thermal Expansion | High | |||||||||
| Heat Resistance (Scaling Strength) | High/High | |||||||||
| Yield Strength | 47000 lbs/in² | |||||||||
| Tensile Strength | 88000 lbs/in² | |||||||||
| Elongation percent in 2 inches | 46 % | |||||||||
| Hardness (Rockwell B) | 85 | |||||||||
| Density | 0.29 lbs/in³ | |||||||||
| Modulus of Elasticity in Tension | 29.0 x 106 lbs/in² | |||||||||
| Specific Heat (32 to 212°F) | 0.12 BTU/ºF/lbs | |||||||||
| Thermal Conductivity at 212°F | 9.0 BTU/hr.ft²/ft/ºF | |||||||||
| Thermal Conductivity at 932°F | 10.8 BTU/hr.ft²/ft/ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 212°F) | 8.3 x 10-6 ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 600°F) | 9.3 x 10-6 ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 1000°F) | 9.6 x 10-6 ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 1200°F) | 10.0 x 10-6 ºF | |||||||||
| Melting Point Range | 2550 to 2650 ºF | |||||||||
| Electrical Resistivity | 78 µΩ.cm | |||||||||
| Max. Operating Temp. (Continuous Service) | 2000 ºF | |||||||||
| Max. Operating Temp. (Intermittent Service) | 1800 ºF | |||||||||
| Welding Properties | Good-Tough Welds | |||||||||
| Drawing and Stamping | Good | |||||||||
| Hot Working - Initial Forging | 2050 to 2250 ºF | |||||||||
| Annealing Temp. | 1850 to 2050 ºF | |||||||||
| Stress Relieving Temp. | 400 to 750 ºF | |||||||||
| Applications |
|
|||||||||
|
|
||||||||||