| Material | Type 316L Stainless Steel | |||||||||
| Shapeform | Round Bar | |||||||||
| Diameter | 1/16 inches | 3/32 inches | 1/8 inches | 5/32 inches | 3/16 inches | |||||
| Diameter | 0.0625 inches1.5875 mm | 0.0938 inches2.38252 mm | 0.125 inches3.175 mm | 0.1563 inches3.97002 mm | 0.1875 inches4.7625 mm | |||||
| Weight | 0.010 lbs/ft0.01488 kg/m | 0.0240 lbs/ft0.035712 kg/m | 0.042 lbs/ft0.062496 kg/m | 0.065 lbs/ft0.09672 kg/m | 0.094 lbs/ft0.139872 kg/m | |||||
| Finish | No. 2B | |||||||||
| Condition | Cold Finished Annealed | |||||||||
| Nominal Composition | 0 to 0.25% Carbon 1.00% Max. Silicon 2.00% Max. Manganese 6 to 36% Nickel 7 to 30% Chrome | |||||||||
| ASTM Specification | ASTM A276 UNS S31603 | |||||||||
| Steel Alloy Group | Austenitic | |||||||||
| Magnetic Properties | Non-Magnetic | |||||||||
| Harden By | Cold Work | |||||||||
| Corrosion Resistance | High | |||||||||
| Hardness | Low to Med. | |||||||||
| Strength | Low to Med. | |||||||||
| Ductility | High | |||||||||
| Toughness | High | |||||||||
| Elec. Conductance | Low | |||||||||
| Thermal Conductance | Low | |||||||||
| Thermal Expansion | High | |||||||||
| Heat Resistance (Scaling Strength) | High/High | |||||||||
| Yield Strength | 45000 lbs/in² | |||||||||
| Tensile Strength | 18200 lbs/in² | |||||||||
| Elongation percent in 2 inches | 50 % | |||||||||
| Hardness (Rockwell B) | 83 | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1000°F | 25000 lbs/in² | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1100°F | 7900 lbs/in² | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1200°F | 7900 lbs/in² | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1300°F | 7900 lbs/in² | |||||||||
| Density | 0.29 lbs/in³ | |||||||||
| Modulus of Elasticity in Tension | 29.0 x 106 lbs/in² | |||||||||
| Specific Heat (32 to 212°F) | 0.12 BTU/ºF/lbs | |||||||||
| Thermal Conductivity at 212°F | 9.04 BTU/hr.ft²/ft/ºF | |||||||||
| Thermal Conductivity at 932°F | 12.4 BTU/hr.ft²/ft/ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 212°F) | 8.9 x 10-6 ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 600°F) | 9.0 x 10-6 ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 1000°F) | 9.7 x 10-6 ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 1200°F) | 10.3 x 10-6 ºF | |||||||||
| Melting Point Range | 2500 to 2550 ºF | |||||||||
| Electrical Resistivity | 74 µΩ.cm | |||||||||
| Max. Operating Temp. (Continuous Service) | 1700 ºF | |||||||||
| Max. Operating Temp. (Intermittent Service) | 1600 ºF | |||||||||
| Welding Properties | Good | |||||||||
| Drawing and Stamping | Good | |||||||||
| Hot Working - Initial Forging | 2100 to 2300 ºF | |||||||||
| Annealing Temp. | 1950 to 2050 ºF | |||||||||
| Stress Relieving Temp. | 400 to 750 ºF | |||||||||
| Applications |
|
|||||||||
|
|
||||||||||