| Items |
 /Asset/Hex-Bars.jpg 316HB-250 Hexagon Stainless Steel Bar - Type 316 |
/Asset/Hex-Bars.jpg 316HB-375 Hexagon Stainless Steel Bar - Type 316 |
/Asset/Hex-Bars.jpg 316HB-4375 Hexagon Stainless Steel Bar - Type 316 |
/Asset/Hex-Bars.jpg 316HB-500 Hexagon Stainless Steel Bar - Type 316 |
/Asset/Hex-Bars.jpg 316HB-5625 Hexagon Stainless Steel Bar - Type 316 |
|||||
| Material | Type 316 Stainless Steel | |||||||||
| Shapeform | Hexagon Bar | |||||||||
| Size | 1/4 inches | 3/8 inches | 7/16 inches | 1/2 inches | 9/16 inches | |||||
| Size | 0.25 inches6.35 mm | 0.375 inches9.525 mm | 0.4375 inches11.1125 mm | 0.5 inches12.7 mm | 0.5625 inches14.2875 mm | |||||
| Weight | 0.1841 lbs/ft0.2739408 kg/m | 0.4142 lbs/ft0.6163296 kg/m | 0.5637 lbs/ft0.8387856 kg/m | 0.7363 lbs/ft1.0956144 kg/m | 0.9318 lbs/ft1.3865184 kg/m | |||||
| Weight per 12' Length | 2.209 lbs1.000677 kg | 4.970 lbs2.25141 kg | 6.765 lbs3.064545 kg | 8.835 lbs4.002255 kg | 11.182 lbs5.065446 kg | |||||
| Finish | No. 2B | |||||||||
| Condition | Cold Drawn Annealed | |||||||||
| Nominal Composition | 0 to 0.25% Carbon 1.00% Max. Silicon 2.00% Max. Manganese 6 to 36% Nickel 7 to 30% Chrome | |||||||||
| ASTM Specification | ASTM A276 UNS S31600 | |||||||||
| Random Length | 10 to 14 ft | |||||||||
| Steel Alloy Group | Austenitic | |||||||||
| Magnetic Properties | Non-Magnetic | |||||||||
| Harden By | Cold Work | |||||||||
| Corrosion Resistance | High | |||||||||
| Hardness | Low to Med. | |||||||||
| Strength | Low to Med. | |||||||||
| Ductility | High | |||||||||
| Toughness | High | |||||||||
| Elec. Conductance | Low | |||||||||
| Thermal Conductance | Low | |||||||||
| Thermal Expansion | High | |||||||||
| Heat Resistance (Scaling Strength) | High/High | |||||||||
| Yield Strength | 45000 lbs/in² | |||||||||
| Tensile Strength | 18200 lbs/in² | |||||||||
| Elongation percent in 2 inches | 50 % | |||||||||
| Hardness (Rockwell B) | 83 | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1000°F | 25000 lbs/in² | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1100°F | 18200 lbs/in² | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1200°F | 12700 lbs/in² | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1300°F | 7900 lbs/in² | |||||||||
| Density | 0.29 lbs/in³ | |||||||||
| Modulus of Elasticity in Tension | 29.0 x 106 lbs/in² | |||||||||
| Specific Heat (32 to 212°F) | 0.12 BTU/ºF/lbs | |||||||||
| Thermal Conductivity at 212°F | 9.4 BTU/hr.ft²/ft/ºF | |||||||||
| Thermal Conductivity at 932°F | 12.4 BTU/hr.ft²/ft/ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 212°F) | 8.8 x 10-6 ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 600°F) | 9.0 x 10-6 ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 1000°F) | 9.7 x 10-6 ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 1200°F) | 10.3 x 10-6 ºF | |||||||||
| Melting Point Range | 2500 to 2550 ºF | |||||||||
| Electrical Resistivity | 74 µΩ.cm | |||||||||
| Max. Operating Temp. (Continuous Service) | 1650 ºF | |||||||||
| Max. Operating Temp. (Intermittent Service) | 1500 ºF | |||||||||
| Welding Properties | Very Good-Tough Welds | |||||||||
| Drawing and Stamping | Good | |||||||||
| Hot Working - Initial Forging | 2100 to 2300 ºF | |||||||||
| Annealing Temp. | 1850 to 2050 ºF | |||||||||
| Stress Relieving Temp. | 400 to 750 ºF | |||||||||
| Applications |
|
|||||||||
|
|
||||||||||