Inconel 601 is nickel-chromium alloy with an addition of aluminum for outstanding resistance to oxidation and other forms of high-temperature corrosion. It also has high mechanical properties at elevated temperatures. Inconel 601 is used for industrial furnaces; heat-treating equipment such as baskets, muffles and retorts; petrochemical and other process equipment; and gas-turbine components. Standard product forms are round, flats, forging stock, pipe, tube, plate, sheet, strip and wire.
Request Information
Unit of Measure
Items
Nickel and High Temperature Alloy Plate

Inconel® 601 Plate
Nickel and High Temperature Alloy Plate

Inconel® 601 Plate
Nickel and High Temperature Alloy Plate

Inconel® 601 Plate
Nickel and High Temperature Alloy Plate

Inconel® 601 Plate
Nickel and High Temperature Alloy Plate

Inconel® 601 Plate
Material N/A Inconel®
Shapeform N/A Plates
Thickness N/A 3/16 inches N/A 1/4 inches N/A 5/16 inches N/A 3/8 inches N/A 1/2 inches
Thickness N/A 0.1875 inches4.7625 mm N/A 0.25 inches6.3500 mm N/A 0.3125 inches7.9375 mm N/A 0.375 inches9.5250 mm N/A 0.500 inches12.7 mm
Plate Weight per Unit Area N/A 0.0595 lbs/in²41.8326412 kg/m² N/A 0.0795 lbs/in²55.8940332 kg/m² N/A 0.0995 lbs/in²69.9554252 kg/m² N/A 0.118 lbs/in²82.9622128 kg/m² N/A 0.156 lbs/in²109.6788576 kg/m²
Alloy N/A Inconel® 601
Basic Composition N/A 1.4% Aluminum 14.4% Iron 23.0% Chrominum 60.5% Nickel
Density N/A 0.291 lbs/in³8.06 g/cm³
ASTM Specification N/A ASME SB-168 ASTM B168 SAE 5870 UNS N06601
Melting Temperature Range N/A 2480 to 2571 ºF1360 to 1411 ºC
Rupture Strength (1000 h at 1200°F/650°C) N/A 28000 psi195 MPa
Rupture Strength (1000 h at 1400°F/760°C) N/A 9100 psi63 MPa
Rupture Strength (1000 h at 1600°F/870°C) N/A 4300 psi30 MPa
Rupture Strength (1000 h at 1800°F/980°C) N/A 2100 psi14 MPa
Rupture Strength (1000 h at 2000°F/1095°C) N/A 1000 psi7 MPa