Aluminum Sheet and Coil - Series 1100-H14

1100 grade is commercially pure aluminum. It is soft and ductile and has excellent workability. It is ideal for applications involving intricate forming because it work hardens more slowly than other alloys. It is the most weldable of aluminum alloys, by any method. It is non heat-treatable. It has excellent resistance to corrosion and is widely used in the chemical and food processing industries. It responds well to decorative finishes which make it suitable for giftware.

1100-H14
Mill Finish
AMS-QQ-A-250/1 AMS4003 ASTM B209

Request Information Search by Specification

Unit of Measure

Items	1100-H14-016-36-C Aluminum Sheet and Coil - Series 1100-H14	1100-H14-020-36-C Aluminum Sheet and Coil - Series 1100-H14	1100-H14-020-96 Aluminum Sheet and Coil - Series 1100-H14	1100-H14-025-36-C Aluminum Sheet and Coil - Series 1100-H14	1100-H14-025-96 Aluminum Sheet and Coil - Series 1100-H14
Material	N/A Aluminum
Shapeform	N/A Coil	N/A Coil	N/A Sheets	N/A Coil	N/A Sheets
Series	N/A 1100-H14
Grade	N/A 1100
Temper	N/A H14
Finish	N/A Mill
Thickness	N/A 0.016 inches0.4064 mm	N/A 0.02 inches0.508 mm	N/A 0.02 inches0.508 mm	N/A 0.025 inches0.6350 mm	N/A 0.025 inches0.6350 mm
Size	N/A 36 x Coil	N/A 36 x Coil	N/A 36 x 96	N/A 36 x Coil	N/A 36 x 96
Width	N/A 36
Length	N/A	N/A	N/A 96	N/A	N/A 96
Sheet Weight per Unit Area	N/A 0.226 lbs/ft²1.103 kg/m²	N/A 0.282 lbs/ft²1.377 kg/m²	N/A	N/A 0.353 lbs/ft²1.723 kg/m²	N/A
Weight per Sheet	N/A	N/A	N/A 6.77 lbs3.071 kg	N/A	N/A 8.47 lbs3.842 kg
Coil Weight per Length	N/A 0.677 lbs/ft1.007 kg/m	N/A 0.847 lbs/ft1.260 kg/m	N/A	N/A 1.058 lbs/ft1.574 kg/m	N/A
ASTM Specification	N/A AMS 4003 AMS-QQ-A-250/1 ASME SB-209 ASTM B209
Ultimate Strength	N/A 18 ksi
Yield Strength	N/A 17 ksi
Elongation percent in 2 inches	N/A 9
Hardness Brinnel Number	N/A 32
Ultimate Shearing Strength	N/A 11 ksi
Fatigue Endurance Limit¹	N/A 7 ksi
Modulus of Elasticity²	N/A 10.0 x 10⁶ ksi
Resistance to Corrosion - General³	N/A A
Stress Corrosion Cracking⁴	N/A A
Workability (Cold)⁵	N/A A
Mechinability	N/A D
Brazeability⁶	N/A A
Gas Weldability⁷	N/A A
Arc Weldability⁸	N/A A
Resistance Spot and Seam Weldability⁹	N/A A
Applications	N/A Sheet metal work, spun hollowware, fin stock
Density	N/A 0.098 lbs/in³
Specific Gravity	N/A 2.71
¹ Based on 500000.000 cycles of completely reversed stress using the R. R. Moore-type of machine and specimen. ² Average of tension and compression moduli. Compression modulus is about 2 percent greater than tension modulus. ³ Ratings A through E are relative ratings in decreasing order of merit, based on exposures to sodium chloride solution by intermittent spraying or immersion. Alloys with A and B ratings can be used in industrial and seacoast atmospheres without protection. Alloys with C, D and E ratings generally should be protected at least on faying surfaces. ⁴ Stress-corrosion cracking ratings are based on service experience and on laboratory tests of specimens exposed to the 3.5% sodium chloride alternate immersion test. ⁵ Ratings A through D for Workability (cold), and A through E for Machinability, are relative ratings in decreasing order of merit. ⁶ Ratings A through D for Weldability and Brazeability are relative ratings. ⁷ A = Generally weldable by all commercial procedures and methods. B = Weldable with special techniques or for specific applications that justify preliminary trials or testing to develop welding procedure and weld performance. C = Limited weldability because of crack sensitivity or loss in resistance to corrosion and mechanical properties. ⁸ A = Generally weldable by all commercial procedures and methods. B = Weldable with special techniques or for specific applications that justify preliminary trials or testing to develop welding procedure and weld performance. C = Limited weldability because of crack sensitivity or loss in resistance to corrosion and mechanical properties. ⁹ A = Generally weldable by all commercial procedures and methods. B = Weldable with special techniques or for specific applications that justify preliminary trials or testing to develop welding procedure and weld performance. C = Limited weldability because of crack sensitivity or loss in resistance to corrosion and mechanical properties.